Braided sleeve for electric cable and its production method
A sleeve and cable technology, applied in the field of cable braided sleeve and its production, can solve the problems of heavy weight, poor flexibility, easy adhesion, etc., and achieve the effects of light weight, wide temperature range and good flexibility
Inactive Publication Date: 2003-04-23
汪建华
View PDF0 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] At present, GB2731 and GB2715 polyvinyl chloride glass fiber sleeves are used for mechanical protection sleeves used in radios, motors, instruments, various circuit wire bundles, and wiring bundles. This product becomes hard and easy to break under low temperature conditions. When the temperature exceeds 32°C, the surface exhibits sticky and easy-to-stick defects, and its weight is heavy and its flexibility is poor. It is not suitable for military weapons used in aerospace, rockets, and aviation, as well as high-precision instruments, electronic electromechanical equipment, and radio testing equipment. used in
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0009] A cable braided sleeve as shown in the attached figure is made of 210D nylon yarn and 0.18mm antimagnetic metal fiber. Among them, the ratio of 210D nylon yarn and 0.18mm antimagnetic metal fiber is 8:1, and its production method is composed of tube making, grouping, weaving, winding molding, and packaging process steps. The weaving process parameters are shown in Table 1. Its products The technical standards are shown in Table 2.
[0010] Nominal inner diameter
[0011] project
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
Description
[0001] The present invention is that the date of application is September 5, 1996, the application number is 96118338.1, and the name of the invention is a divisional application of the patent application for cable braided sleeve and production method thereof. technical field [0002] The invention relates to a cable sleeve and a production method thereof, in particular to a cable braided sleeve and a production method thereof. Background technique [0003] At present, GB2731 and GB2715 polyvinyl chloride glass fiber sleeves are used for mechanical protection sleeves used in radios, motors, instruments, various circuit wire bundles, and wiring bundles. This product becomes hard and easy to break under low temperature conditions. When the temperature exceeds 32°C, the surface exhibits sticky and easy-to-stick defects, and its weight is heavy and its flexibility is poor. It is not suitable for military weapons used in aerospace, rockets, an...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine