Method for manufacturing forming die for optical element, forming die for optical element and optical element

A technology for optical components and forming molds, used in optical components, manufacturing tools, optics, etc., can solve the problems of long-term use of peeling, coating and low affinity for ceramics

Inactive Publication Date: 2012-04-11
KONICA MINOLTA OPTO
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, there is a problem that the affinity between the plating layer and the ceramic is relatively low, and problems such as peeling may occur when used for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing forming die for optical element, forming die for optical element and optical element
  • Method for manufacturing forming die for optical element, forming die for optical element and optical element
  • Method for manufacturing forming die for optical element, forming die for optical element and optical element

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] In order to achieve the above object, the preferable structure thereof is explained below.

[0017] The method of manufacturing a molding die for an optical element described in item 1 is characterized in that a film layer of an amorphous metal having a supercooled liquid region is formed on the surface of a mold base material having a heat conductivity of 1 to 20 W / mK , the supercooled liquid region contains more than 20-80mol% selected from Pt, Ir, Au, Pd, Ru, Rh, Fe, Co, Ni, Zr, Al, Ti, Cu, W, Mo, Cr, B, P At least one or more elements, by performing predetermined processing on the surface of the film layer, form the optical surface of the mold (referred to as the surface that is transferred to form the optical surface of the optical element to be formed).

[0018] For example, when attaching an electroless Ni plating layer on the surface of a mold base material and forming the optical surface of the mold on it, it takes a very long time of several weeks to obtain th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a forming mold for an optical element, comprising a mold formed by material having 1- 20W / mK thermoconductivity and an amorphous metal film layer formed on the mold basic material having an undercooling liquid region, the undercooling liquid region comprises at least one element selected from Pt, Ir, Au, Pd, Ru, Rh, Fe, Co, Ni, Zr, Al, Ti, Cu, W, Mo, Cr, B, P whcihthe mol is above 20-80mol%, the mold optical surface is formed by preliminarily processing the surface of the film layer.

Description

technical field [0001] The present invention relates to a method of manufacturing a molding die for optical elements capable of shortening the molding cycle, a molding die for optical elements manufactured by the manufacturing method, and an optical element formed by the molding die for optical elements. Background technique [0002] According to the manufacturing method of molds for molding plastic optical elements generally practiced in the prior art, for example, Fe-based materials such as steel or stainless steel are used to manufacture blanks (primary processed products), and electroless plating called electroless nickel plating is performed on them. , forming an alloy coating of amorphous nickel and phosphorus with a thickness of about 100 μm. This coating is cut with an ultra-precision machining machine using a diamond tool to form a high-precision optical surface transfer surface for forming the optical surface of an optical element. [0003] However, in recent year...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C33/38C03B11/08C23C14/06C23C14/24C23C14/34C23C14/48C23C16/00G02B1/00G02B3/00
CPCC03B2215/11C03B2215/16C03B11/086
Inventor 汤浅清司细江秀和田一启
Owner KONICA MINOLTA OPTO