Calcium sulphoaluminate-alite composite mineral phase cement clinker and its preparation method
A technology of calcium sulfoaluminate and cement clinker, which is applied in the field of cement materials and can solve problems such as unfavorable large-scale production, unstable clinker mineral composition, and large performance differences.
Inactive Publication Date: 2007-04-25
李金洪
View PDF6 Cites 18 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] Using the above method, the composition of clinker minerals is unstable, an
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0081] Example 1: design MG=1.05, MS=0.95; ingredients: fly ash 23.91%, bauxite 9.34%, limestone 58.61%, gypsum 7.41%, fluorite 0.74%, firing temperature 1250°C.
Embodiment 2
[0082] Example 2: design MG=1.05, MS=0.95; ingredients: fly ash 23.91%, bauxite 9.34%, limestone 58.61%, gypsum 7.41%, fluorite 0.74%, firing temperature 1300°C.
Embodiment 3
[0083] Example 3: design MG=1.00, MS=1.00; ingredients: fly ash 25.84%, bauxite 7.50%, limestone 58.51%, gypsum 7.41%, fluorite 0.74%, firing temperature 1250°C.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention discloses calcium sulphoaluminate-Relit composite mineral phase cement and preparing method, which is characterized by the following: adopting coal ash, alumina, limestone and plaster as raw material and fluorite as mineralizer; designing MG and MS value; introducing new Relit mineral in the preparing course of common aluminium sulfate cement; preparing new clinker of new calcium sulphoaluminate-Relit composite mineral phase cement under 1200-1330 deg.c with 45%-65% C4A3S, 20%-36% C3S and residual C2S.
Description
technical field [0001] The invention belongs to the technical field of cement materials and relates to the preparation of novel calcium sulfoaluminate-alite composite mineral phase cement clinker with fly ash as the main raw material. Background technique [0002] Calcium sulfoaluminate and alite are the main mineral phases of ordinary sulfoaluminate cement and Portland cement, respectively. Calcium sulfoaluminate has good gelling properties and fast hydration speed, and is a typical early-strength mineral, but the later-stage strength growth rate is low; Alite mineral is also a mineral with excellent gelling properties, which is the strength of Portland cement. The main source, but the early strength is low, and the late strength increase rate is high. Therefore, realizing the combination of these two main minerals in sulfoaluminate cement and Portland cement to prepare a new type of calcium sulfoaluminate-alite composite mineral phase cement can further improve the mechan...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
IPC IPC(8): C04B7/00C04B7/32C04B7/02C04B7/36
CPCC04B7/32
Inventor 李金洪赵宏伟
Owner 李金洪
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap