Coating solution for forming ultraviolet-absorbing film, and ultraviolet-absorbing glass article
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Image
Examples
example 1
[0137]41.9 g of ethanol, 17.3 g of tetramethoxysilane, 5.8 g of 3-glycidoxypropyltrimethoxysilane, 15.0 g of the silylated ultraviolet absorber-solution obtained in the above Preparation Example, 15.8 g of pure water and 4.2 g of 1% nitric acid aqueous solution were charged and stirred for one hour to obtain a coating solution 1 for forming an ultraviolet-absorbing film. Then, the coating solution 1 was applied by a spin coating method on a high heat-absorbing green glass having its surface cleaned (Tv: 75.2%, Tuv: 9.5%, transmittance of light with a wavelength of 380 nm: 38.5%, 10 cm in length, 10 cm in width, 3.5 cm in thickness, tradename: UVFL, manufactured by Asahi Glass Company, Limited) and dried in atmospheric air at 150° C. for 30 minutes, to obtain an ultraviolet-absorbing film-attached glass plate. The properties of the obtained ultraviolet-absorbing film-attached glass plate were evaluated as follows. The evaluation results are shown in Table 2.
[Evaluations]
[0138]1) Film...
example 2
[0145]An ultraviolet ray-absorbing film-attached glass plate was prepared in the same manner as in Example 1 except that the film thickness was changed. The properties of the obtained ultraviolet-absorbing film-attached glass plate were evaluated in the same manner as in Example 1. The evaluation results are shown in Table 2.
example 3
[0146]42.6 g of ethanol, 18.1 g of tetramethoxysilane, 4.6 g of 3-glycidoxypropyltrimethoxysilane, 14.8 g of the silylated ultraviolet absorber solution obtained in the above Preparation Example, 15.8 g of pure water and 4.2 g of a 1% nitric acid aqueous solution were charged and stirred for one hour to obtain a coating solution 2 for forming an ultraviolet-absorbing film. An ultraviolet-absorbing film-attached glass plate was prepared in the same manner as in Example 1 except that the above coating solution 2 was used instead of the coating solution 1. The properties of the obtained ultraviolet-absorbing film-attached glass plate were evaluated in the same manner as in Example 1. The evaluation results are shown in Table 2.
PUM
Property | Measurement | Unit |
---|---|---|
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap