Environmental protection inorganic powder material and polymer composite modified emulsification asphalt grouting material

A technology of inorganic powder materials and emulsified asphalt, which is applied to the materials used in waterproofing and reinforcement projects, and in the field of expressway maintenance and maintenance. It can solve problems such as insufficient performance, short duration, and poor overall effect, and achieve excellent high temperature stability. , prolong the service life, and improve the waterproof effect

Inactive Publication Date: 2010-01-06
陈宪宏 +3
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved in the present invention is, in order to overcome the performance deficiency that exists in the grouting material (cement+fly ash+water glass etc.) that is used for reinforcing and waterproofing treatment to existing road at present, adopt traditional grouting material to road Due to the poor overall effect and short duration after the reinforcement treatment, repeated repairs and maintenance are often required. An environmentally friendly inorganic powder material and polymer composite modified emulsified asphalt grouting material, including filling and strengthening grouting material, is proposed. And waterproof grouting material, which does not break the emulsion during pressure grouting and has good groutability during construction; the grouting material can not only meet the base reinforcement and surface waterproofing of rigid pavement (cement pavement) by changing the proportion, but also It can meet the requirements of base reinforcement and surface waterproofing of asphalt pavement, and has comprehensive properties such as excellent wear resistance, strength, aging resistance, excellent waterproof effect and good permeability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental protection inorganic powder material and polymer composite modified emulsification asphalt grouting material
  • Environmental protection inorganic powder material and polymer composite modified emulsification asphalt grouting material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: Inorganic powder material and polymer composite modified emulsified asphalt for rigid pavement are used for filling and supplementing strong grouting material, and its composition in parts by weight is: emulsified asphalt: inorganic powder material: protective agent=30:70 : 15.

[0022] The emulsified asphalt is commercially available, and its solid content is in the range of 30wt.%-70wt.%.

[0023] The composition of the inorganic powder material (active material) in parts by weight is: cement: mineral powder: quartz sand = 6:2:2 and uniformly mixed.

[0024] The mass ratio of the protective agent is composed of: cationic rubber powder: polymer emulsion: polyethylene glycol: bentonite: defoamer: amphoteric surfactant: calcium chloride: water=100:200:100:400:1:4 : 10:80; wherein the cationic rubber powder is cationic acrylate rubber powder, the polymer emulsion is cationic acrylate emulsion, the defoamer is silicone powder defoamer, and the amphoteric sur...

Embodiment 2

[0026] Embodiment 2: Inorganic powder material and polymer composite modified emulsified asphalt filling and reinforcing grouting material, its composition in parts by weight is: emulsified asphalt: inorganic powder material: protective agent = 35:70:15.

[0027] The parts by weight of the inorganic powder material (active material) consist of: cement: mineral powder: fly ash=6: 2: 2 uniformly mixed to get final product; described emulsified asphalt and protective agent, production process are all the same as in Example 1 same.

Embodiment 3

[0028] Example 3: Inorganic powder material and polymer composite modified emulsified asphalt waterproof grout, its composition in parts by weight is: emulsified asphalt: inorganic powder material: protective agent = 70:30:20.

[0029] The parts by weight of the inorganic powder material (active material) components consist of: cement: mineral powder: fly ash = 6:3:3 and mix it uniformly to get final product; the emulsified asphalt and protective agent, production process All the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is emulsified asphalt grouting material modified with inorganic powder and polymer. The modified emulsified asphalt grouting material may be filling and reinforcing grouting material comprising emulsified asphalt in 25-35 weight portions, inorganic powder in 65-75 weight portions and protecting agent in 10-20 weight portions; or waterproof grouting material comprising emulsified asphalt in 65-75 weight portions, inorganic powder in 25-35 weight portions and protecting agent in 10-30 weight portions. The modified emulsified asphalt grouting material has high grouting performance, high transmission capacity, no demulsification during pressure grouting, high binding with interface, high curing speed, excellent waterproof effect and other advantages. It may be applied for highway maintenance, foundation stabilization and waterproof engineering.

Description

technical field [0001] The invention relates to a material mainly used in highway and construction industry, especially in the repair and maintenance of expressway, as well as waterproof and reinforcement engineering in construction industry. Background technique [0002] With the rapid increase of traffic flow and the continuous increase of the tonnage of heavy-duty vehicles, the wear and tear on the road surface and the damage to the base layer of the road surface are greatly increased than before. After the joint filling material failed, the rainwater continued to infiltrate into the base layer. Under the influence of its own weight and the gravity of the vehicle, there was a serious gap between the base layer and the concrete plate in some sections of the road, resulting in cracks, cracks, cracks, and cracks in the road surface plate. Breakage, breakage, damage, etc. In addition, the erosion and hollowing of rain (snow) water can easily cause cracks on the road surface;...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26C04B28/00C04B18/08C04B14/04
CPCY02W30/91
Inventor 陈宪宏何美艳袁航黄林冲
Owner 陈宪宏