Copper-base catalyst alloy with anti-scaling function and preparation method thereof

An alloy and functional technology, applied in the field of copper-based catalyst alloy with anti-scaling function and its preparation, can solve problems such as affecting the normal operation of industrial production, paralysis of production system, equipment explosion, etc.

Active Publication Date: 2010-01-27
JINTAN HENGXU TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the water treatment process of petroleum, chemical industry, electric power, papermaking, printing and dyeing, heating and other industries, as well as in the process of water heating, water pipelines must be used. Water pipelines will produce scale during long-term high-temperature use. This substance The occurrence of these accidents will affect the normal operation of industrial production in light cases, and lead to the paralysis of the entire production system or major safety accidents such as equipment explosions in severe cases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The copper-based catalyst alloy with anti-scaling function is composed of eight metal elements Cu, Ni, Zn, Sn, Pb, Fe, Sb, and Mn, and the weight percentage of each component is: Cu40%; Ni15%; Zn20%; Sn15%; Pb4%; Fe4%; Sb1%; 100 A columnar crystal alloy with oriented crystal axis growth, which can prevent scale formation and has the ability to dissolve scale.

Embodiment 2

[0011] The copper-based catalyst alloy with anti-scaling function has eight metal elements including Cu, Ni, Zn, Sn, Pb, Fe, Sb, and Mn, and the weight percentage of each component is: Cu60%; Ni10%; Zn15%; Sn8%; Pb2%; Fe3%; Sb1%; Mn1%.

Embodiment 3

[0013] The copper-based catalyst alloy with anti-scaling function is composed of eight metal elements Cu, Ni, Zn, Sn, Pb, Fe, Sb, and Mn, and the weight percentage of each component is: Cu70%; Ni5%; Zn10%; Sn10%; Pb1%; Fe3%; Sb0.5%; Mn0.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a copper base catalyst alloy capable of antiscaling, the alloy is made from Cu, Ni, Zn, Sn, Pb, Fe, Sb and Mn eight elements under high temperature, the invention further discloses the preparation of the alloy. By the formula and preparation of the invention, a styloid alloy which orientated grows along S100 crystal axis is acquired, the alloy can prevent scale forming, as well as dissolve scale.

Description

Technical field: [0001] The invention relates to a formula of a copper-based catalyst alloy material with anti-scaling function and a preparation method thereof. Background technique: [0002] In the water treatment process of petroleum, chemical industry, electric power, papermaking, printing and dyeing, heating and other industries, as well as in the process of water heating, water pipelines must be used. Water pipelines will produce scale during long-term high-temperature use. This substance The occurrence of these accidents will affect the normal operation of industrial production in light cases, and cause major safety accidents such as paralysis of the entire production system or explosion of equipment in severe cases. For a long time, people have been conducting scientific research to find new metal materials with anti-fouling properties. Invention content: [0003] The object of the invention is to provide a copper-based catalyst alloy material with anti-scaling fu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/00C22C30/06C22C1/02
Inventor 鲁礼民刘东刘寺意
Owner JINTAN HENGXU TECH