Production of fast-drying water self-stripping metal heat treatment protecting coating

A technology for metal heat treatment and protective coatings, applied in the field of preparation of water-based self-stripping metal heat treatment protective coatings, can solve the problems of slow drying of coatings, metal decarburization and oxidation, and non-environmental protection, and achieve good metal adhesion and coating dense effect

Inactive Publication Date: 2007-11-21
SHANGHAI JIAO TONG UNIV
View PDF1 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Metal heat treatment is generally performed at a high temperature of 400∽2000°C. If the metal is not protected during physical heat treatment, the metal will be decarburized and oxidized; during chemical heat treatment, if the part that does not need to penetrate elements is not protected, the metal parts will be scrapped.
[0003] The first way to solve the above problems is to protect the metal surface by copper plating, which has complicated procedures, high cost and is not environmentally friendly; the second is to coat the metal surface with a heat treatment protective coating
Generally, the existing protective coatings for metal heat treatment are mainly composed of glass, ceramics, and silicates, but these coatings are slow to dry and have poor adhesion to metals. Machining allowance, for precision machining, this type of coating is difficult to meet the requirements of machining accuracy
[0004] Metal heat treatment protective film such as the "Preparation Method of Metal Heat Treatment Protective Film" disclosed in Chinese Patent Application No. 85102501, its composition includes rubber, gasoline, benzene and boric acid, first make adhesive with rubber, gasoline or benzene, and then prepare protective film with boric acid film, which can wrap the protective film on the metal workpiece; although the metal protection effect of the protective film is good and it can fall off automatically, there are toxic or flammable solvents such as gasoline and benzene in the preparation, and it is not suitable for complex shapes. metal workpiece

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0015] (1), preparation of quick-drying water-based self-stripping metal heat treatment protective coating:

[0016] According to the formula described in Table 1, disperse boric acid, water-based resin, titanium dioxide paste, colored pigment paste, defoamer, and deionized water in a stainless steel tank with a stirrer at high speed until the fineness is less than 50 μ. After passing the inspection, filter, Measuring, packaging.

[0017] raw material

Example 1

Example 2

Example 3

Example 4

boric acid

45.0

50.0

55.5

60.0

Solid content 50wt%, Tg35℃propylene

acid emulsion

45.0

Solid content 55wt%, Tg40℃ styrene

Acrylic Emulsion

40.0

Solid content 35wt%, Tg-30℃ water

permanent polyurethane resin

35.0

Solid content 60wt%, Tg55℃ styrene

Butadiene Emulsion

36.0

70wt% titanium dioxide, 10wt% polysulfone

Titanium dioxide with 20wt% deio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for producing fast-dry water self-stripping metal heat-treatment protective coating is carried out by putting boric acid 40.0-70.0 wt%, water resin 25.0-50.0 wt%, titanium pigment slurry 1.0-15.0 wt%, coloring pigment slurry 0.1-10.0 wt%, de-foaming agent 0.1-2.0 wt% and de-ionized water residue into stainless steel jar, high-speed dispersing to fineness below 50mu by agitator, filtering and packing to obtain final product. The precision metal work pieces have excellent oxidation and de-carbonizing resistances with air as medium for physical heat treatment, and have excellent cementation, aluminizing, siliconing and chromizing resistances with chemical substances as medium for chemical heat treatment. It has brushing and spraying functions, fast dry speed and better adhesion.

Description

Technical field: [0001] The invention relates to the field of mechanical processing metal heat treatment protection, in particular to a preparation method of a quick-drying water-based self-stripping metal heat treatment protection coating. Background technique: [0002] The metal heat treatment process can be divided into physical heat treatment and chemical heat treatment. Physical heat treatment such as normalizing, quenching, and annealing is to achieve the mechanical properties required by the workpiece by changing the transformation of the metal crystal phase structure; chemical heat treatment is through other chemical elements such as carbon and nitrogen. , aluminum, silicon, sulfur, cyanide, etc., to change the chemical composition of the metal surface, and then undergo subsequent heat treatment to achieve special performance requirements such as mechanical properties, chemical properties, and process properties. Metal heat treatment is generally performed at a high ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21D1/68
Inventor 罗漫
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products