Gravure rubber wheel directly transfer printing pattern metallic plate

A metal plate and template technology, applied in the direction of metal layered products, metal material coating process, superimposed layer plating, etc. The effect of product cost

Inactive Publication Date: 2007-11-28
HAIER GRP CORP +1
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] In summary, the existing technology is applied to the problem that pattern printing cannot be realized on the surface of ordinary color-coated steel sheets for home appliances and architectural decoration, especially gravure printing. In view of this, the present invention is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gravure rubber wheel directly transfer printing pattern metallic plate
  • Gravure rubber wheel directly transfer printing pattern metallic plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042]In this embodiment, the printing process is as follows, a gravure roll 1, the gravure roll 1 is immersed in the printing ink storage tank 6 to continuously coat the ink, the gravure roll 1 after the ink is dipped Use the scraper 2 to scrape off excess ink, and the ink pattern on the gravure roller 1 is transferred to the surface of the printing rubber roller 3, and the printing rubber roller 3 prints the ink pattern on its surface on the steel plate 7, and the other side of the steel plate is provided with a Support roller 4.

Embodiment 2

[0044] In this embodiment, the printing process is as follows, a gravure roll 1, the gravure roll 1 is immersed in the printing ink storage tank 6 to continuously coat the ink, the gravure roll 1 after the ink is dipped Use the scraper 2 to scrape off the excess ink, the ink pattern on the gravure roller 1 is transferred to the surface of the printing rubber roller 3, and the printing rubber roller 3 prints the ink pattern on its surface on the steel plate 7, and the support of the steel plate 7 is on the plane On the support transmission belt 5, on the other side of the printing rubber roller 3, a cleaning roller 9 is arranged, and the cleaning roller 9 is immersed in the washing tank 8 and is continuously cleaned. Another doctor blade 2 is arranged on the printing rubber roller 3 .

[0045] In the steel plate printing process of the present invention, if the ink printing lines are not clear, a cleaning roller can be added at the position of the printing rubber roller.

[00...

Embodiment 3

[0051] After the resin and ink are mixed in the following ratio, that is, resin Medium:black ink=3:1, the viscosity of their mixture under the 5# cup is 18 seconds.

[0052] 20

40

60

80

100

viscosity

17.22

13.48

12

10.8

10.25

[0053] Through research, the direction of the researchers of the present invention, the preferred solvent ratio, adopts the ratio of common type solvent: slow-drying solvent=1:1.

[0054] Under the condition that described ink of the present invention has been proportioned, preferred printing conditions are as follows:

[0055] (1) Drying temperature: 180 degrees;

[0056] (2) SP value (surface tension) above 13;

[0057] (3) The continuous coating and printing process speed for steel coils can reach 15-40 m / min, and the printing process speed for single steel plates can reach 5-20 m / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention is printed metal plate with intaglio offset transfer printed patterns and its making process. On the surface of coated steel sheet, patterns are first printed with ink fitting the surface coating of steel sheet and through intaglio offset printing, and high temperature cured paint or UV cured paint is then roller coated to the surface of the patterns. The printed metal plate has high decorating effect. Compared with available technology, the present invention has the advantages of environment friendship and low cost.

Description

technical field [0001] The invention belongs to the field of color printed metal plates used for housings of household appliances, interior and exterior decoration of buildings, etc., and particularly relates to a steel plate suitable for various bending, impacting, stretching and other sheet metal processing after indirect printing with gravure rubber rollers and a manufacturing method thereof. Background technique [0002] At present, colored metal plates used in the market for housings of household appliances and interior and exterior decoration of buildings, such as refrigerator shells, refrigerator side panels, microwave oven shells, air conditioner shells, washing machine shells, etc., generally use colored pre-painted steel plates and colored laminated steel plates. [0003] The color pre-coated steel plate adopts the following structure: the base material is made of steel plates such as cold-rolled plate, electro-galvanized plate, hot-dip galvanized plate, galvanized ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44C5/04B05D5/00B32B15/08C23C28/00
Inventor 赵秀娟郭长秋付强李留军齐思潮王鹏
Owner HAIER GRP CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap