Sole mould and method for making the same

A shoe sole mold and mold technology, which is applied to household appliances, other household appliances, household components, etc., can solve the problems of increasing the manpower and time of the mold, and achieve the effect of reducing manpower and cost.

Inactive Publication Date: 2010-05-12
YUE DEAN TECH CORP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the manufacturing method of this kind of shoe sole mold not only needs to process and shape the metal substrates of the upper and lower molds respectively, but also needs to carry out surface treatment on the processed and shaped upper and lower molds, so the manpower and labor required for mold making are relatively increased. time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sole mould and method for making the same
  • Sole mould and method for making the same
  • Sole mould and method for making the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention is a kind of shoe sole mold 10 and its preparation method, please refer to figure 1 , figure 2 As shown, its preparation method includes:

[0029] 1. Mold 10 molding: firstly carry out curved surface processing on a single metal base material 40, and then the upper mold 20 and the lower mold 30 of the designed sole are structured as follows figure 2 As shown, the metal substrate 40 after curved surface processing is casted, the structure of the lower mold 30 is formed on one side of the metal substrate 40, and the upper mold 20 is formed on the other side, and the metal substrate after casting The surface of the material 40 is polished, wherein the metal base 40 can be a zinc-tin alloy;

[0030] 2. Mold 10 cutting: For the metal substrate 40 after casting figure 2 It is cut in the manner shown, so that the metal substrate 40 is cut to form the required upper mold 20 and lower mold 30 respectively;

[0031] 3. Mold 10 processing: the upper m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a sole mould and making method, wherein, the making method which comprises a mould molding, that is, after a metal parent material is processed on curved surface, the upper and lower moulds of the sole are molded on the metal parent material, therefore, the structure of the lower mould is molded on one side of the metal parent material, while the upper mould is molded on the other side of the metal parent material, and a mould cutting, that is, the molded metal parent material is cut for processing, therefore, the cut metal parent material is the demanded upper and lower moulds and a mould processing, that is, a combination apparatus is used to combine the cut upper mould and the lower mould. The metal parent material of the sole mould is zinc tin alloy. The invention can mold quickly the needed sole mold, thereby effectively reducing the needed labor power and cost.

Description

technical field [0001] The invention relates to a shoe sole mold and a manufacturing method thereof. Background technique [0002] The sole molding of current shoes is formed by injecting or injecting plastic into the mold, and the general form of the mold 60 is composed of an upper mold 61 and a lower mold 62, and the plastic is poured into the space between the upper mold 61 and the lower mold 62. In the mold cavity and then die forming, and the forming of the upper mold 61 and the lower mold 62 is as follows: image 3 As shown, wherein the two metal substrates 70 forming the moulds are respectively cast and molded to form an upper mold 61 and a lower mold 62 respectively, and the upper mold 61 and the lower mold 62 after casting are respectively subjected to surface polishing treatment, That is, the existing shoe sole mold 60 is formed. [0003] However, the manufacturing method of this kind of shoe sole mold not only needs to process and shape the metal substrates of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/24B29C33/38B29L31/50
Inventor 张景昇陈尚志
Owner YUE DEAN TECH CORP