Chromium-free fingerprint-resistant coating

A anti-fingerprint and coating technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve environmental hazards, chromium pollution and other problems, and achieve the effects of improving fingerprint resistance, short curing time, and improving hot stickiness and cold brittleness

Active Publication Date: 2010-06-09
JIANGSU LANLING POLYMER MATERIAL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the problem that the existing chromium-containing anti-fingerprint coatings will cause certain harm to the environment during preparation, storage, transportation and use, especially the problem of chromium pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0013] The specific composition and proportioning of a kind of preferred anti-fingerprint paint are as follows:

[0014] components

[0015] Add 600g of water-based polyurethane resin to the reaction kettle, add 70g of silicon dioxide water-based sol, 100g of water-based polytetrafluoroethylene wax slurry while stirring, add 20g of ethylene glycol, and then put EFTOPEF-112 2g and Adeka into the reaction kettle NATE B-1019 5g, and finally add 203g of deionized water into the reaction kettle, and continue stirring for 15 minutes to obtain the product No. 1 chrome-free anti-fingerprint coating.

example 2

[0017] The specific composition and proportion of a kind of anti-fingerprint paint are as follows:

[0018] components

[0019] components

[0020] Add 1000g of water-based polyurethane resin to the reaction kettle, add 120g of silicon dioxide water-based sol, 300g of water-based polytetrafluoroethylene wax slurry while stirring, then add 60g of ethylene glycol, and then put EFTOPEF-112 2g and Adeka into the reaction kettle NATE B-1019 6g, and finally add 500g of deionized water into the reaction kettle, and continue stirring for 15 minutes to obtain the product No. 2 chrome-free anti-fingerprint coating.

example 3

[0022] The chrome-free anti-fingerprint coating prepared in example one and example two is carried out full performance test, and test result is as follows:

[0023] serial number

project

Chromium-free anti-fingerprint paint No. 1

Chromium-free anti-fingerprint paint No. 2

index

1

viscosity

7

10

8±3cps(25℃)

2

Fineness

9

6

≤10μm

3

Solvent Composition

Deionized water

Deionized water

Deionized water

4

detergent

Deionized water

Deionized water

Deionized water

5

weight solids

23.4％

24.5％

25±2(％)

6

volume solids

24.8％

25.1％

24±2(％)

7

Wet film specific gravity

1.06

1.04

1.03±0.05

8

Dry film specific gravity

1.09

1.11

1.07±0.05

9

Dry film thickness

0.9

1.2

1±0.5μm

10

storage period

6 months

6 months

6 months

11

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention is capable to settle the problems that existing fingerprint-proof paints containing chrome cause certain hazard to the environment during the preparation, storage and transportation, particularly to settle the problem of chrome pollution. The invention involves the following chemical compositions: water urethane resin (40 to 70wt percent), silicon dioxide sols (4 to 8wt percent), water teflon wax-dispersion (10 to 20wt percent), deionized water (20 to 40wt percent), EFTOP EF-112 (0.2 to 0.3wt percent), glycol (2 to 3wt percent) and Asekahate B-1019 (0.5 to 0.7wt percent).Water urethane resin is injected in to a reaction kettle, the silicon dioxide and water teflon wax-dispersion are added (agitating at the same time), and film-forming assistant is added, and then other assistants are put into the reaction kettle, and finally, the deionized water is added into the reaction kettle. The fingerprint-proof paint is achieved by agitating continuously for 15 to 30 minutes.

Description

technical field [0001] The invention relates to a coating composition, in particular to an anti-fingerprint coating for manufacturing anti-fingerprint steel plates. Background technique [0002] At present, as people's requirements for quality of life are getting higher and higher, not only are the daily necessities used beautiful, but they are also required to be environmentally friendly and harmless. With the continuous update of automobiles, home appliances, office supplies, etc., the requirements for steel plates are getting higher and higher. Fingerprint-resistant steel plates are an upgraded product and high value-added surface treatment product. Compared with ordinary bare steel plates, it is not only The corrosion resistance of the steel plate is improved, and there are many new properties such as fingerprint resistance, coating and electrical conductivity. In the existing technology, the anti-fingerprint steel plate treatment is to passivate the substrate wire and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/00
Inventor 高新田马金庄建林
Owner JIANGSU LANLING POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap