Chromium-free fingerprint-resistant coating

A fingerprint-resistant and coating technology, used in polyurea/polyurethane coatings, coatings, etc., can solve problems such as chromium pollution and environmental hazards, and achieve the effects of improving fingerprint resistance, short curing time, and improving hot sticking and cold brittleness.

Active Publication Date: 2008-02-13
JIANGSU LANLING POLYMER MATERIAL CO LTD
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the problem that the existing chromium-containing anti-fingerprint coatings will cause certain harm to the environment during preparation, storage, transportation and use, especially the problem of chromium pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0013] The specific composition and proportioning of a kind of preferred anti-fingerprint paint are as follows:

[0014] components

[0015] Add 600g of water-based polyurethane resin to the reaction kettle, add 70g of silicon dioxide water-based sol, 100g of water-based polytetrafluoroethylene wax slurry, and then add 20g of ethylene glycol, and then put EFTOPEF-1122g and Adeka NATE into the reaction kettle B-10195g, finally add 203g of deionized water into the reaction kettle, and continue to stir for 15 minutes to obtain the product No. 1 chrome-free anti-fingerprint coating.

example 2

[0017] The specific composition and proportion of a kind of anti-fingerprint paint are as follows:

[0018] components

[0019] Ethylene glycol

[0020] Add 1000g of water-based polyurethane resin to the reaction kettle, add 120g of silica water-based sol, 300g of water-based PTFE wax slurry while stirring, and then add 60g of ethylene glycol, and then put EFTOPEF-1122g and Adeka NATE into the reaction kettle B-10196g, finally add 500g deionized water into the reaction kettle, and continue to stir for 15 minutes to obtain the product No. 2 chrome-free anti-fingerprint coating.

example 3

[0022] The chrome-free anti-fingerprint coating prepared in example one and example two is carried out full performance test, and test result is as follows:

[0023] Numbering

project

Chromium-free anti-fingerprint paint No. 1

Chromium-free anti-fingerprint paint No. 2

indicators

1

viscosity

7

10

8±3cps(25℃)

2

Fineness

9

6

≤10μm

3

Solvent Composition

Deionized water

Deionized water

Deionized water

4

detergent

Deionized water

Deionized water

Deionized water

5

weight solids

23.4％

24.5％

25±2(％)

6

volume solids

24.8％

25.1％

24±2(％)

7

Wet film specific gravity

1.06

1.04

1.03±0.05

8

Dry film specific gravity

1.09

1.11

1.07±0.05

9

Dry film thickness

0.9

1.2

1±0.5μm

10

storage period

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention aims to solve the harm to the environment caused by the existing chromium-containing anti-fingerprint coatings in the process of preparation, storage, transportation and use, especially the pollution caused by chromium to the environment. The chemical components involved in the present invention are: water-based polyurethane resin 40~70wt%, silica sol 4~8wt%, water-based polytetrafluoroethylene wax paste 10~20wt%, deionized water 20~40wt%, EFTOP EF-112 0.2~0.3wt%, ethylene glycol 2~3wt% %, Asekahate B-1019 0.5~0.7wt%, put water-based polyurethane resin into the reaction kettle, add silicon dioxide, water-based PTFE wax slurry while stirring, then add film-forming aids, and then put into the reaction kettle For other additives, add deionized water into the reaction kettle at last, and continue to stir for 15 to 30 minutes to obtain the product chrome-free anti-fingerprint coating.

Description

technical field [0001] The invention relates to a coating composition, in particular to an anti-fingerprint coating for manufacturing anti-fingerprint steel plates. Background technique [0002] At present, as people's requirements for quality of life are getting higher and higher, not only are the daily necessities used beautiful, but they are also required to be environmentally friendly and harmless. With the continuous update of automobiles, home appliances, office supplies, etc., the requirements for steel plates are getting higher and higher. Fingerprint-resistant steel plates are an upgraded product and high value-added surface treatment product. Compared with ordinary bare steel plates, it is not only The corrosion resistance of the steel plate is improved, and there are many new properties such as fingerprint resistance, coating and electrical conductivity. In the existing technology, the anti-fingerprint steel plate treatment is to passivate the substrate wire and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D5/00
Inventor 高新田马金庄建林
Owner JIANGSU LANLING POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com