Water base ink for inkjet recording
An inkjet recording, water-based technology, applied in ink, applications, household appliances, etc., can solve problems such as unsatisfactory rub resistance, and achieve the effect of excellent rub resistance and high printing density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
manufacture example 1 and 2
[0209] In the reaction vessel, 20 parts of methyl ethyl ketone and 0.03 parts of polymer chain transfer agent (2-mercaptoethanol), 10% of 200 parts of the monomer mixture shown in Table 1 were added and mixed, and nitrogen replacement was fully carried out to obtain a mixed solution.
[0210] On the other hand, the remaining 90% of the monomer mixture shown in Table 1 was added to the dropping funnel, 0.27 parts of the above-mentioned polymer chain transfer agent (0.17 parts in Production Example 2), 60 parts of methyl ethyl ketone and 1.2 parts of A radical polymerization initiator (2,2'-azobis(2,4-dimethylvaleronitrile)) (1.1 parts in Production Example 2) was mixed together, and nitrogen substitution was sufficiently performed to obtain a mixed solution.
[0211] Under a nitrogen atmosphere, while stirring the mixed solution in the reaction vessel, the temperature was raised to 65° C., and the mixed solution in the dropping funnel was slowly added dropwise over 3 hours. Aft...
Embodiment 1
[0221] 25 parts of polymer obtained by drying the polymer solution obtained in Production Example 1 under reduced pressure were dissolved in 70 parts of methyl ethyl ketone, and 4.1 parts of neutralizing agent (5N aqueous sodium hydroxide solution) (neutralization degree 75%) and 230 parts were added thereto. Parts of ion-exchanged water, neutralized to form a salt base, and then add 75 parts of diazo pigment (yellow: Y) (C.I. Pigment Yellow 74 [P.Y.74], the average primary particle size is 40nm, manufactured by Sanyo Pigment Co., Ltd., Product name: FY7413), using Asada Iron Works (Co., Ltd.) ピコミル (dispersion medium: zirconium dioxide, temperature: 20 ° C, dispersion medium / dispersion liquid weight ratio: 8 / 2), at a peripheral speed of 15m / s, carry out 2 hours for dispersion. The obtained mixture was subjected to dispersion treatment 10 times by a Microfluidizer (manufactured by Microfluidics corp., trade name) under a pressure of 200 MPa.
[0222] Add 250 parts of ion-exc...
Embodiment 2
[0225] Aqueous ink 2 was obtained in the same manner as in Example 1, except that the processing conditions of Asada Tekko Co., Ltd. Picomil were changed to a peripheral speed of 8 m / s and a processing time of 12.5 hours.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap