Method for making hydrophobic solution and hydrophobic glass

A manufacturing method and technology for water-repellent glass, which are applied in the fields of water-repellent liquid and water-repellent glass, can solve the problems of blurred vision and car accidents, and achieve broad application prospects, reduced maintenance costs, and good friction resistance.

Inactive Publication Date: 2003-08-13
FUYAO GLASS IND GROUP CO LTD
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in rainy and snowy weather, a layer of water film is formed on the surface of the glass, resulting in blurred vision, especially for car drivers, which often leads to car accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Preparation scheme of hydrophobic liquid for ordinary tempered glass or ordinary float glass cured at room temperature:

[0028] (a) Tridecafluorooctyltriethylsilane CF 3 (CF 2 ) 5 C 2 h 4 Si(OC 2 h 5 ) 3 5%

[0029] (b) Orthoethyl silicate Si(OC 2 h 5 ) 4 1%

[0030] (c) Absolute ethanol C 2 h 5 OH 94%

[0031] Then add 3% deionized water and 0.4% hydrochloric acid with a concentration of 37% to the solution, mix and stir for 20 hours.

[0032] Hydrophobic glass method:

[0033] (1) Clean the glass:

[0034] Scrub it with water, dry it, and then clean it with a cleaning agent. After cleaning, rinse until there is no cleaning agent residue, and then dry it;

[0035] (2) prepare hydrophobic solution;

[0036] (3) Coating hydrophobic film:

[0037] Apply the above-mentioned hydrophobic liquid evenly on the outer surface of the glass (spray, dip, or smear); then dry the surface with a towel or paper towel, and the amount of th...

Embodiment 2

[0041] Preparation scheme of hydrophobic liquid for car windshield solidified under high temperature environment:

[0042] (a) Tridecafluorooctyltriethylsilane CF 3 (CF 2 ) 5 C 2 h 4 Si(OC 2 h 5 ) 3 0.8%

[0043] (b) Orthoethyl silicate Si(OC 2 h 5 ) 4 1.5%

[0044] (c) Absolute ethanol C 2 h 5 OH 97.7%

[0045] Then add 2% deionized water and 0.2% hydrochloric acid with a concentration of 37% to the solution, mix and stir for 15 hours.

[0046] Hydrophobic treatment of laminated glass for front windshield of automobiles is divided into five stages:

[0047] (1) Clean the outer sheet of the bent original sheet of laminated glass.

[0048] The processing method is the same as in Embodiment 1.

[0049] (2) prepare hydrophobic solution;

[0050] (3) coating hydrophobic film; same as above

[0051] (4) curing

[0052] Put the glass at 320°C for 10 minutes, and the hydrophobic liquid will react with the glass surface to form a firm hydropho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A process for preparing a hydrophobic solution and a hydrophobic glass used for the windscreen of car is disclosed. Said hydrophobic solution is prepared from CF3(CF2)5C2H4Si(OC2H5)3, Si(OC2H5)4, C2H5OH, deionized water, and hydrochloric acid through proportional mixing, and stirring for 5-20 hr. Said hydrophobic glass is prepared through cleaning glass, preparing said hydrophobic solution, coating it on the surface of glass, and solidifying at 250-350 deg.C for 10 min -72 hr to form a firm hydrophobic film.

Description

Technical field: [0001] The patent of the invention belongs to the field of glass processing, and in particular relates to a hydrophobic liquid and a method for manufacturing hydrophobic glass. Background technique: [0002] Existing automotive glass is made of float glass or general flat glass. Water has wettability to float glass or general flat glass, because the surface tension of glass is 4 times greater than that of water, that is, the surface of glass has higher surface energy. The glass used in various industries or the products processed from this kind of glass, such as automobile glass, does not have the function of water repellency. Therefore, in rainy and snowy weather, a layer of water film is formed on the surface of the glass, resulting in blurred vision, especially for car drivers, which often leads to car accidents. Invention content: [0003] The object of the present invention is to provide a kind of water-repellent liquid, and utilize it to manufactur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C17/00C03C17/30
Inventor 戴克攻张兴卢国水王鸿飞
Owner FUYAO GLASS IND GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com