Thermoplastic polyolefin-like waterproof material and preparation method thereof

A thermoplastic polyolefin, waterproof material technology, applied in building insulation materials, chemical instruments and methods, other chemical processes, etc., can solve the problems of low tensile strength, poor aging performance, environmental pollution, etc., to achieve high tensile strength, Good puncture resistance and convenient construction

Active Publication Date: 2012-07-04
上海申达科宝新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, said TPO material also has certain deficiencies, such as: low tensile strength, generally only 20Mpa; especially its poor dimensional stability after the finished product, close to and exceeding 1.5%, therefore, it needs to be modified to meet the needs of waterproof materials
However, waterproof materials made of EPDM, chlorinated polyethylene-rubber blends, rubber-plastic blends, and reclaimed rubber are prone to aging, and carbon black reinforcement is generally required during processing. , so the environmental pollution is serious; and the waterproof materials made of polyvinyl chloride (PVC) and chlorinated polyethylene (CPE) also have poor aging performance, especially the need to add plasticizers, which may become brittle due to the migration of plasticizers The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic polyolefin-like waterproof material and preparation method thereof
  • Thermoplastic polyolefin-like waterproof material and preparation method thereof
  • Thermoplastic polyolefin-like waterproof material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] preparation figure 1 The thermoplastic polyolefin waterproofing material shown.

[0034] Warp-knitted polyester fabric is used as the base fabric, with a total thickness of 2.0mm;

[0035] The warp fineness of the base fabric is 1000D, the weft fineness is 1000D, and the weave density is: 9 warp threads / cm, 9 weft threads / cm

[0036] The material of the bottom layer is a dark layer, the thickness of which is 40% of the total thickness of the waterproof material, the thickness of the performance improvement layer is 20% of the total thickness of the waterproof material, and the surface layer is 30% of the total thickness;

[0037] Components and parts by weight of each layer:

[0038] Surface layer

modified layer

bottom layer

TPO

100

100

100

Polymer modified material

5

25

15

Fill modifier

5

40

10

lubricant

0.2

0.4

0.2

Antioxidants

...

Embodiment 2

[0054] preparation figure 1 The thermoplastic polyolefin waterproofing material shown.

[0055] Warp-knitted polyester fabric is used as the base fabric, with a total thickness of 0.8mm;

[0056] The warp fineness of the base fabric is 250D, the weft fineness is 250D, and the tissue density is: 6 warp threads / cm, 6 weft threads / cm; the material of the bottom layer is a dark layer, and the thickness is 20% of the total thickness of the waterproof material. The thickness of the said performance improvement layer is 40% of the total thickness of the waterproof material, and the surface layer is 40% of the total thickness;

[0057] Components and parts by weight of each layer:

[0058] Surface layer

modified layer

bottom layer

TPO

100

100

100

Polymer modified material

15

15

25

Fill modifier

20

20

30

lubricant

0.3

0.6

0.3

Antioxidants

2

0

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides thermoplastic polyolefine waterproofing material and a preparation method thereof. The waterproofing material takes warp-knitting terylene cloth (1) as base cloth, a surface course (4) is coated on the upper side surface of the base cloth (1), and a performance improvement layer (2) and a bottom layer (3) are orderly coated on the lower side surface of the base cloth (1). The thermoplastic polyolefine waterproofing material of the invention has good processing performance and mechanical performance and the recovery and reuse performance which the EPDM does not possess, can realize the body welding, contain no plasticiser in the auxiliary materials, have no problem of getting brittle due to the migration of the plasticizer, have the comprehensive characteristics of large tensile strength, good puncture resistance, strong ultraviolet resistance, smooth surface, high reflectivity, pollution resistance and so on, also have the characteristics of easy processing, weldability, convenient construction and complete recovery during the engineering application, and is the novel green environmental protection waterproofing material.

Description

technical field [0001] The invention relates to a waterproof material, in particular to a waterproof material mainly composed of thermoplastic polyolefins. Background technique [0002] With the popularization and development of various modern buildings and related technologies, the demand for waterproof materials in the field of construction engineering is increasing, and the quality requirements for them are getting higher and higher. Residential construction is one of the important factors for the growth of demand for waterproof materials, and roof maintenance and building renovation projects will also become another huge market space for waterproof materials. [0003] At present, in various waterproof materials at home and abroad, polymer-based materials are used, mainly EPDM, polyvinyl chloride (PVC), chlorinated polyethylene (CPE), chlorinated polyethylene Ethylene-rubber blends, rubber-plastic blends and recycled polyethylene (PE) geomembranes, etc. [0004] Thermop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/18B32B33/00B32B27/32E04B1/64
Inventor 胡淳曹庆辉李捷钱建华张贤德李平凡
Owner 上海申达科宝新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products