Acoustic absorption, noise insulation, thermal insulation, condensation resistant building material, preparation method and application thereof
A building material and anti-condensation technology, applied in the field of building materials, can solve the problems of greater harm to the human body and the surrounding environment, no anti-condensation function, and condensation on indoor surfaces, so as to shorten the echo reflection time, light weight, The effect of improving the overall sound insulation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0034] Component I is a water-based interface agent, purchased from Jilin Kelong Decoration Co., Ltd., product name: KL-Tj-5 water-based interface agent, composed of epoxy-modified acrylic resin, modifiers, and additives.
[0035] The preparation of component II: take each component by following weight: 100% log pulp 60kg, binder (vinyl acrylic acid 75%, emulsion 15%, remainder is water) 40kg, fire retardant 5kg; The raw wood pulp is mixed with the binder and the fire retardant, and stirred evenly to obtain the product;
[0036] Component III: consists of 70wt% component I, 15wt% emulsion, and the balance is water, wherein the component I is composed of any one of styrene, butyl acrylate, silane or methyl methacrylate Or a mixture of more than one in any proportion;
[0037] The above three components are individually packaged.
Embodiment 2
[0039] Component I is a water-based interface agent, purchased from Jilin Kelong Decoration Co., Ltd., product name: KL-Tj-5 water-based interface agent, composed of epoxy-modified acrylic resin, modifiers, and additives.
[0040] The preparation of component II: take each component by following weight: 100% log pulp 66kg, binding agent (vinyl acrylic acid 70%, emulsion 10%, remainder is water) 35kg, fire retardant 2kg; The raw wood pulp is mixed with the binder and the fire retardant, and stirred evenly to obtain the product;
[0041]Component III: composed of 60wt% of component I, 5wt% of emulsion, and the balance of water, wherein the component I is composed of any one of styrene, butyl acrylate, silane or methyl methacrylate Or a mixture of more than one in any proportion;
[0042] The above three components are individually packaged.
Embodiment 3
[0044] Component I is a water-based interface agent, purchased from Jilin Kelong Decoration Co., Ltd., product name: KL-Tj-5 water-based interface agent, composed of epoxy-modified acrylic resin, modifiers, and additives.
[0045] Preparation of Component II: Take each component by the following weight: 55kg of 100% raw wood pulp, 45kg of binder (80% vinyl acrylic acid, 15% of emulsion, and the remainder is water), 2kg of fireproofing agent, 0.5kg of mildewproofing agent kg; mix 100% raw wood pulp with binder, fireproofing agent and antifungal agent, stir evenly, and obtain;
[0046] Component III: consists of 75wt% component I, 20wt% emulsion, and the balance is water, wherein the component I is composed of any one of styrene, butyl acrylate, silane or methyl methacrylate Or a mixture of more than one in any proportion;
[0047] The above three components are individually packaged.
PUM
Property | Measurement | Unit |
---|---|---|
flame retardant | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com