Sulfotetraphenyl porphyrin nano luminescent material and preparation method thereof

A technology of sulfonic acid tetraphenyl porphyrin and monosulfonic acid tetraphenyl porphyrin, which is applied in the field of porphyrin nano-fluorescent materials and its preparation, and can solve the problem that the size of nano-sheets and nano-blocks is large, and the difficulty of process and operation is increased. , single-shaped nanoparticles, etc., to achieve the effect of low production cost, simple method and good small size effect

Inactive Publication Date: 2009-03-18
CHONGQING UNIV +1
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this method are: (1) only nanoparticles with a single shape can be obtained; (2) a stabilizer needs to be added, which increases the difficulty of the process and operation; (3) increases the production cost; (4) will bring certain pollution
The main disadvantages of this method are: (1) surfactants need to be added, which increases the difficulty of the process and operation; (2) increases the production cost; (3) will bring certain pollution
The nanosheets and nanoblocks prepared by this method are relatively large in size, and the monosulfonic tetraphenylporphyrin (TPPS) prepared under the conditions described in this method is relatively large. 1 ) The fluorescence intensity of nanomaterials is only TPPS 1 About 8 times that of the monomer (see attached figure 1 ), the intensity is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sulfotetraphenyl porphyrin nano luminescent material and preparation method thereof
  • Sulfotetraphenyl porphyrin nano luminescent material and preparation method thereof
  • Sulfotetraphenyl porphyrin nano luminescent material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A monosulfonic tetraphenylporphyrin (TPPS 1 ) The nano fluorescent material is a fluorescent nano sheet with a rectangular cross-section, 400-450nm in length and 200-300nm in width.

[0035] A monosulfonic tetraphenylporphyrin (TPPS 1 ) The concrete steps of the preparation method of nanometer material are as follows:

[0036] (1)TPPS 1 Configuration of ethanol solution

[0037] TPPS 1 Place it in a container, add ethanol solution, and stir evenly with a stirrer to prepare TPPS 1 TPPS with mass concentration of 0.58mmol / L 1 Ethanol solution, stored at 3°C ​​in the dark, for later use.

[0038] (2)TPPS 1 Preparation of Nano Fluorescent Material Dispersion System

[0039] After step (1) is completed, press TPPS 1 Ethanol solution: the volume ratio of three distilled water is the ratio of 1:60, the TPPS prepared and preserved in step (1) 1 The ethanol solution is injected into triple distilled water with an initial temperature of 3°C through the injector, then he...

Embodiment 2

[0045] A monosulfonic tetraphenylporphyrin (TPPS1) nano fluorescent material, which is a fluorescent nanosheet with a rectangular cross section of 350-450nm in length and 150-300nm in width and a fluorescent nanosheet with a length of 500-850nm and a width of 70-90nm Fluorescent nanostrips.

[0046] A monosulfonic tetraphenylporphyrin (TPPS 1 ) The concrete steps of the preparation method of nanometer material are as follows:

[0047] (1)TPPS 1 Configuration of ethanol solution

[0048] With embodiment 1, feature is: prepare TPPS 1 The mass concentration is 0.43mmol / L, and the storage temperature in the dark is 4°C.

[0049] (2)TPPS 1 Preparation of nano-fluorescent materials

[0050] With embodiment 1, feature is: TPPS 1 The volume ratio of ethanol solution: triple distilled water is 1:50, the initial temperature of triple distilled water is 4°C, the temperature of the mixture is 70°C, the stirring speed is 1600rpm, and the stirring time is 10 minutes.

[0051] (3) Ce...

Embodiment 3

[0056] A monosulfonic tetraphenylporphyrin (TPPS 1 ) nano fluorescent material, which is a fluorescent nanosheet with a rectangular cross section, 350-400nm in length and 150-250nm in width.

[0057] A monosulfonic tetraphenylporphyrin (TPPS 1 ) The concrete steps of the preparation method of nanometer material are as follows:

[0058] (1)TPPS 1 Configuration of ethanol solution

[0059] With embodiment 1, feature is: prepare TPPS 1 The mass concentration is 0.50mmol / L, and the storage temperature in the dark is 4°C.

[0060] (2)TPPS 1 Preparation of nano-fluorescent materials

[0061] With embodiment 1, feature is: TPPS 1 The volume ratio of ethanol solution: triple distilled water is 1:70, the initial temperature of triple distilled water is 4°C, the temperature of the mixed solution is kept constant at 4°C, the stirring speed is 1550rpm, and the stirring time is 15 minutes.

[0062] (3) Centrifugal separation

[0063] With embodiment 1, feature is: the speed of cen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sulfonic acid tetraphenyl porphyrin nano-fluorescent material and a preparation method thereof, which relate to a fluorescent porphyrin material and a preparation method thereof. The sectional shape of the material is of a rectangular sheet or strip or sheet and strip. The method comprises the following steps: preparing a TPRS alcohol solution first, preparing a TPPS nano-fluorescent material dispersion system, and obtaining a product through separation and drying. The material has smaller size and better photosensitivity, has good characteristics of a porphyrin monomer such as rigidity and flexibility, electronic buffer capacity, photosensitivity, high chemical stability, wide spectral response, and also has special properties after the nanometer treatment such as small-size effect, surface effect, quantum effect, interfacial effect. The method is simple, has low production cost, and is convenient for promotion and application. The material prepared by adopting the method can be widely used as markers, photosensitive materials as well as sensitive recognition elements and materials for constructing photoelectric devices, molecular devices and sensors.

Description

technical field [0001] The invention belongs to the technical field of porphyrin nanometer materials, in particular to a porphyrin nanometer fluorescent material and a preparation method thereof. Background technique [0002] Nanotechnology is another major technology that profoundly affects social and economic development after information technology and biotechnology. Its rapid development will bring about a revolutionary change in almost all industrial fields in the 21st century. Nanomaterials have physical and chemical properties that traditional materials do not have: small size effect, surface effect, quantum effect and interface effect. So that it has some special properties that ordinary materials do not have: lead to new small size effects in physical properties such as sound, light, electromagnetic, and thermodynamics; as the particle diameter becomes smaller, the specific surface area will increase significantly. Such a high specific surface makes the number of a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/06B82B3/00
Inventor 侯长军向芸颉霍丹群法焕宝罗小刚时晓杰
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com