Uvioresistant, antibacterial and flame retardant terylene fiber, preparation method and application thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A flame-retardant polyester and anti-ultraviolet technology, applied in the field of polyester fiber, to achieve the effect of improving spinnability, reasonable process and wide application range
Active Publication Date: 2011-06-15
微笑纺织科技(太仓)有限公司
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] At present, people are developing products in the fields of anti-ultraviolet, antibacterial or flame retardant, but they are limited to unilaterally modifying fibers for anti-ultraviolet, antibacterial or flame retardant, and cannot solve how to organically combine the three to obtain a wide range of multifunctional applications. fiber
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] 1. An anti-ultraviolet, antibacterial, and flame-retardant polyester fiber, which is composed of the following raw materials: 10 kg of silver-based antibacterial masterbatch, 10 kg of anti-ultraviolet masterbatch, and 980 kg of copolymerized phosphorus-based flame-retardant polyester fiber-forming resin.
[0024] 2. Preparation of anti-ultraviolet, antibacterial and flame-retardant polyester fibers:
[0025] (1) Get 10% by weight of nano-silver ions and nano-carrier silicon dioxide and 90% by weight of polyethylene terephthalate blend, extrude with a screw extruder, pelletize, and make silver It is an antibacterial masterbatch, ready for use, wherein the blending temperature is 250°C, and the screw speed is 100rpm;
[0026] (2) take the anti-ultraviolet agent of 10% by weight and the polyethylene terephthalate of 90% by weight, blend, extrude with screw extruder, pelletize, make anti-ultraviolet masterbatch, Standby, wherein the blending temperature is 250°C, and the s...
Embodiment 2
[0040] 1. An anti-ultraviolet, antibacterial and flame-retardant polyester fiber, which is composed of the following raw materials: 100 kg of silver-based antibacterial masterbatch, 50 kg of anti-ultraviolet masterbatch, and 850 kg of copolymerized phosphorus-based flame-retardant polyester fiber-forming resin.
[0041] 2. Preparation of anti-ultraviolet, antibacterial and flame-retardant polyester fibers:
[0042] (1) Get 30% by weight of nano-silver ions and nano-carrier zirconium phosphate to blend with 70% by weight of polyethylene terephthalate, extrude with a screw extruder, and pelletize to obtain silver-based Antibacterial masterbatch, spare, wherein the blending temperature is 270°C, and the screw speed is 190rpm;
[0043] (2) take the anti-ultraviolet agent of 30% by weight and the polyethylene terephthalate of 70% by weight, blend, extrude with screw extruder, pelletize, make anti-ultraviolet masterbatch, Standby, wherein the blending temperature is 270°C, and the ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
oxygen index
aaaaa
aaaaa
elongation at break
aaaaa
aaaaa
coefficient of variation of linear density
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses an uvioresistant, antibacterial and flame retardant terylene fiber, a preparation method and an application thereof. The terylene fiber comprises the following raw materials in percentage by weight: 1-10 percent of silver series antibacterial parent granule, 1-5 percent of uvioresistant parent granule and 85-98 percent of copolymerized type phosphorus flame retardant terylene fiber forming resin. The uvioresistant, antibacterial and flame retardant terylene fiber , the component proportions of which are scientific and reasonable, is prepared by the following steps: scientifically and organically combining the antibacterial silver series parent granules, the uvioresistant parent granules and the copolymerized type phosphorus flame retardant terylene fiber forming resin; preparing a pre-oriented yarn; and then elasticizing and deforming the pre-oriented yarn to produce low-elasticity deformed yarn; thus the terylene fiber has wide range of application. The preparation method of the uvioresistant, antibacterial and flame retardant terylene fiber has strong operability, reasonable process and high production efficiency and can realize industrial mass production.
Description
technical field [0001] The invention relates to a polyester fiber, in particular to an anti-ultraviolet, antibacterial and flame-retardant polyester fiber, a preparation method thereof and an application thereof. Background technique [0002] In recent years, the advancement of science and technology has promoted the development of the chemical fiber industry. Many countries have invested a lot of manpower, material and financial resources to develop new fiber products and search for new polymer materials. There have been breakthroughs in the research and development of various functional fibers. With the advancement of technology, functional fibers with high technological content have become an important factor to guide the market and improve the viability of enterprises. [0003] As one of the three main fibers in synthetic fibers, polyester fiber is widely used in clothing fabrics and other non-clothing fields because of its excellent physical and chemical properties. It...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More