Mining high durability light sprayed concrete

A shotcrete and durability technology, applied in the field of concrete, can solve the problems of dust pollution, inappropriate ratio of raw materials and high rebound rate

Inactive Publication Date: 2010-01-27
SHANXI JINCHENG ANTHRACITE COAL MINING GRP CO LTD
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In order to solve the problems of dust pollution and high rebound rate caused by inappropriate raw material ratio existing in the existing shotcrete technology, the present invention provides a kind of highly durable lightweight shotcrete for mining

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1, the high-durability lightweight shotcrete used for planting mines is composed of the following raw materials in weight ratio: 337.5kg of cement, 737kg of slag, 574kg of sand, 45kg of fly ash, 45kg of slag micropowder, 22.5kg of silica fume, quick-setting Agent 13.5kg, water 180kg.

[0020] After the above raw materials are mixed, they can be directly sprayed on the working surface through the spraying machine. The polyphenylene particles are preferably regenerated polystyrene particles, which are crushed from waste polystyrene boards in a foam crushing granulator, and the characteristics are that the regenerated polyphenylene particles are broken and have a rough surface.

[0021] The particle size of aggregate slag used in the lightweight shotcrete is 2.35-10 mm, and water retention treatment is required before use. The regenerated polyphenylene particles used in the lightweight shotcrete have a particle size of 3-5 mm and a bulk density of 11 kg / m 3 , ...

Embodiment 2

[0027] Embodiment 2, a kind of high-durability lightweight shotcrete for mining is composed of the following raw materials in weight ratio: 320 parts of cement, 750 parts of slag, 590 parts of sand, 50 parts of fly ash, 40 parts of slag micropowder, silica fume 25 parts, 10 parts of accelerator, 200 parts of water. Implementation method is the same as embodiment 1

Embodiment 3

[0028] Embodiment 3, a kind of high-durability lightweight shotcrete for mining is composed of the following raw materials in weight ratio: 350 parts of cement, 710 parts of slag, 590 parts of sand, 40 parts of fly ash, 50 parts of slag micropowder, silica fume 20 parts, 15 parts of accelerator, 160 parts of water. Implementation method is the same as embodiment 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a concrete, in particular to a mining high durability light sprayed concrete, aiming at solving the problems of dust pollution caused by improper mixture ratio of raw materials, high resilience rate and the like in the prior art of the sprayed concrete. The sprayed concrete comprises the raw materials based on the parts by weight: 320-350 parts of cement, 710-750 parts of furnace slag, 550-590 parts of sand, 40-50 parts of pulverized fuel ash, 40-50 parts of mineral waste residue micro powder, 20-25 parts of siliceous dust, 10-15 parts of accelerating agent and 160-200 parts of water. Compared with the common sprayed concrete, the sprayed concrete using light aggregate has the self weight to be reduced by 25-35%, has the mechanical property meeting the tunnel supporting protection need under a certain density grade, and is beneficial to the protection of a whole supporting protection system.

Description

technical field [0001] The invention relates to concrete, in particular to a high-durability lightweight shotcrete for mining. Background technique [0002] Shotcrete construction technology is often used in the mining process. Whether the technology is reasonable or not determines the quality of construction. Many details involved in construction are related to ensuring the strength of shotcrete. Optimal construction technology and reasonable selection of concrete are The key to quality control. Shotcrete construction process mainly includes: dry spraying method, tidal spraying method, wet spraying method, mixed spraying method, etc. [0003] The main difference between them is that the feeding procedures of each process flow are different, especially the timing of adding water and accelerator is different. The dry spraying method is the earliest spraying construction method, and it is widely used. The dry spraying method is to use a forced mixer to dry mix a certain pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B14/06C04B18/14C04B18/08C04B18/12
CPCC04B2111/00146C04B28/02C04B2111/00724C04B20/026C04B2111/40Y02W30/91C04B14/06C04B18/08C04B18/141C04B18/146C04B2103/12
Inventor 付俊青赵军罗树琼尚玮玮管学茂都海龙余洪会
Owner SHANXI JINCHENG ANTHRACITE COAL MINING GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com