High-gloss and high-impact resistance PS / PP composite for manufacturing telephone case and preparation method thereof

A composite material and high-gloss technology, which is applied in the field of manufacturing telephone casing materials and its preparation, can solve the problem of high price, achieve the effects of improved weather resistance, high impact resistance production process, and improved thermal oxidation resistance

Inactive Publication Date: 2012-06-13
ANHUI KEJU NEW MATERIALS
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to propose a PS / PP composite material with high surface gloss, high impact resistance and low price in view of the high price of existing telephone casing materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The present invention proposes a high-gloss, high-impact PS / PP composite material used for manufacturing a telephone casing, which is made of the following raw materials in parts by weight:

[0047] 100 parts of GPPS resin, 20 parts of copolymerized PP resin, 5 parts of nano-montmorillonite, 3 parts of styrene-butadiene-styrene block copolymer, 0.1 part of β crystal nucleating agent 390, (2,4 di 0.1 part of a mixture of tert-butylphenyl)phosphite triester and tetrakis[β-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]pentaerythritol ester; hindered amine UV of Cyasorb -3346 is 0.1 part; zinc stearate is 0.2 part.

[0048] The preparation method comprises the following steps:

[0049] Step 1: taking raw materials according to the above parts by weight;

[0050] Step 2: Mix the raw materials weighed in step 1 in a high-speed mixer for 3 minutes;

[0051] Step 3: Place the mixed components in a parallel twin-screw extruder for melt extrusion and granulation.

[0052] ...

Embodiment 2

[0054] The present invention proposes a high-gloss, high-impact PS / PP composite material used for manufacturing a telephone casing, which is made of the following raw materials in parts by weight:

[0055] 100 parts of GPPS resin, 30 parts of copolymerized PP resin, 8 parts of nano-montmorillonite, 5 parts of styrene-butadiene-styrene block copolymer, 0.3 part of β crystal nucleating agent 390, (2,4 di 0.3 parts of a mixture of tert-butylphenyl)phosphite triester and tetrakis[β-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]pentaerythritol ester; hindered amine UV of Cyasorb -3346 is 0.15 parts; zinc stearate is 0.4 parts.

[0056] The preparation method comprises the following steps:

[0057] Step 1: taking raw materials according to the above parts by weight;

[0058] Step 2: Mix the raw materials weighed in step 1 in a high-speed mixer for 4 minutes;

[0059] Step 3: Place the mixed components in a parallel twin-screw extruder for melt extrusion and granulation.

[0060...

Embodiment 3

[0062] The present invention proposes a high-gloss, high-impact PS / PP composite material used for manufacturing a telephone casing, which is made of the following raw materials in parts by weight:

[0063] 100 parts of GPPS resin, 35 parts of copolymerized PP resin, 9 parts of nano-montmorillonite, 5.5 parts of styrene-butadiene-styrene block copolymer, 0.4 part of β crystal nucleating agent 390, (2,4 di 0.4 parts of a mixture of tert-butylphenyl)phosphite triester and tetrakis[β-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]pentaerythritol ester; hindered amine UV of Cyasorb -3346 is 0.18 parts; zinc stearate is 0.5 parts.

[0064] The preparation method comprises the following steps:

[0065] Step 1: taking raw materials according to the above parts by weight;

[0066] Step 2: Mix the raw materials weighed in step 1 in a high-speed mixer for 4 minutes;

[0067] Step 3: Place the mixed components in a parallel twin-screw extruder for melt extrusion and granulation.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-gloss and high-impact resistance PS / PP composite for manufacturing a telephone case and a preparation method thereof. The composite is mainly prepared by the following raw materials by weight portion: 100 portions of PS resin, 20-60 portions of PP resin, 5-15 portions of compatilizer, 3-30 portions of flexibilizer, 0.1-0.9 portion of nucleator and 0.1-0.9 portion of antioxidant. The PS raw material and the PP raw material are fused together by the special compatilizer. The prepared composite has the high-gloss and high-impact resistance features and excellent physical and mechanical properties, and can be used for replacing ABS to manufacture the telephone case. The composite has the characteristics of simple preparation technology, stable size, high gloss, high impact resistance, low cost, and the like.

Description

technical field [0001] The invention relates to a material for manufacturing a telephone casing and a preparation method thereof, in particular to a PS / PP composite material with high surface gloss and high impact resistance and a preparation method thereof. Background technique [0002] Polystyrene (PS) and polypropylene (PP) are one of the five general-purpose plastics. PS is colorless, odorless, easy to color, rigid, non-toxic, no fungus growth, easy to process, good dimensional stability, low hygroscopicity, and good radiation resistance. But its disadvantages are poor heat resistance, intolerance to boiling water, brittleness, low impact strength, and the products are prone to self-cracking due to internal stress. [0003] PP is the only general-purpose plastic that can be boiled in water. It has excellent chemical stability, outstanding ductility, bending fatigue resistance, easy processing, and low production cost. However, the disadvantages of PP are the disadvanta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L23/14C08L53/02C08K13/02C08K3/34C08K5/521B29B9/00B29C47/92B29C48/40B29C48/92
CPCB29C48/04B29C48/40
Inventor 石立明
Owner ANHUI KEJU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap