Abrasion-resistant and friction-reducing emulsion and preparation method for spraying same on surface of soft metal

A soft metal and emulsion technology, which is applied to the surface coating liquid device, special surface, pre-treated surface, etc., can solve the problems of easy intrusion into soft metal substrates, sharp corner burrs of matching parts, low hardness, etc., and achieve coating Reasonable thickness, improved anti-friction ability, improved wear resistance

Inactive Publication Date: 2010-09-15
LUZHOU GUOBANG MACHINERY
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the low hardness of this kind of soft metal, it is easy to invade the soft metal matrix, cause scratches, and grooves to make it invalid due to the sharp corner burrs of the fittings and hard objects entering the friction part during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Abrasion-resistant and friction-reducing emulsion and preparation method for spraying same on surface of soft metal
  • Abrasion-resistant and friction-reducing emulsion and preparation method for spraying same on surface of soft metal
  • Abrasion-resistant and friction-reducing emulsion and preparation method for spraying same on surface of soft metal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Wear-resistant anti-friction emulsion 1 is composed of the following components by weight percentage:

[0045] PTFE emulsion 50

[0046] Chromium oxide 4.2

[0047] Phosphoric acid 5.4

[0048] Sodium lauryl sulfate 0.4

[0049] distilled water 40

[0050] Such as figure 1 As shown, the above-mentioned wear-resistant and anti-friction emulsion is sprayed on the soft metal surface according to the following preparation steps:

[0051] 1. Parts processing: process soft metals according to the requirements of the drawings, and the thickness of the surface to be sprayed should be reduced to the thickness of the coating.

[0052] 2. To prepare wear-resistant and anti-friction emulsion, add the sodium lauryl sulfate in the ratio of this embodiment into the polytetrafluoroethylene emulsion, and then drop the mixed solution of phosphoric acid, chromium oxide and distilled water into lauryl sulfuric acid Sodium and polytetrafluoroethylene emulsion mixture, while stirring c...

Embodiment 2

[0062] Wear-resistant anti-friction emulsion 2, consisting of the following components by weight percentage:

[0063] PTFE emulsion 69

[0064] Chromium oxide 5.9

[0065] Phosphoric acid 4.9

[0066] Sodium lauryl sulfate 0.2

[0067] distilled water 20

[0068] The preparation method of above-mentioned wear-resisting friction-reducing emulsion 2 spraying on soft metal surface is the same as embodiment 1

Embodiment 3

[0070] Wear-resistant friction-reducing emulsion 3, consisting of the following components by weight percentage:

[0071] PTFE emulsion 60

[0072] Chromium oxide 2

[0073] Phosphoric acid 2.5

[0074] Sodium lauryl sulfate 0.3

[0075] Distilled water 35.2

[0076] The preparation method of spraying the above-mentioned wear-resistant and friction-reducing emulsion 3 on the soft metal surface is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses abrasion-resistant and friction-reducing emulsion. The abrasion-resistant and friction-reducing emulsion comprises 50 to 69 parts of polytetrafluoroethylene emulsion, 2.0 to 5.9 parts of chromium oxide, 2.5 to 5.4 parts of phosphoric acid, 0.2 to 0.4 part of lauryl sodium sulfate, 0.5 to 3.0 parts of abrasion-resistant additive and 20 to 40 parts of distilled water. The invention also relates to a preparation method for spraying the abrasion-resistant and friction-reducing emulsion on the surface of a soft metal. The method comprises the following steps of: preparing the abrasion-resistant and friction-reducing emulsion with the components; treating the surface of soft metal matrix; spraying the emulsion on the surface of the soft metal; drying the soft metal; sintering the soft metal; and quenching the soft metal. When the abrasion-resistant and friction-reducing emulsion of the technical scheme of the invention is coated on the surface of the soft metal, the friction coefficient can be reduced by 20 percent, and the abrasion amount ratio of the soft metal to the basis material is less than or equal to 0.5. The abrasion-resistant and friction-reducing emulsion can be widely used for surface treatment of the soft metal such as copper, aluminum and alloy thereof and the like at a friction and abrasion part of a gear pump side plate, a bearing bush, a bearing block hole, a cylinder barrel and the like, and has novel structure and originality.

Description

technical field [0001] The present invention relates to a wear-resistant and anti-friction emulsion, and also relates to a preparation method for spraying the wear-resistant and anti-friction emulsion on a metal surface, in particular to a kind of soft material with low hardness and good yield and compliance. A method for preparing a wear-resistant and anti-friction coating on a metal surface. Background technique [0002] Copper, aluminum and their alloys, as well as low-hardness metals or alloy materials (soft metals) such as low-carbon steel and low-alloy steel (soft metals) have good running-in performance and reducing friction between friction fittings due to their good concession and compliance. friction performance. Therefore, this kind of soft metal is often used in conjunction with tempered or quenched steel parts, and is widely used in moving friction parts, such as gear pump side plates, bearing bushes, bearing housing holes, cylinders, etc. However, due to the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/18C09D7/12B05D5/08B05D3/02B05D3/12
Inventor 刘邦友郑国群
Owner LUZHOU GUOBANG MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap