Method for producing synthetic rutile by using deluvial slope type ilmentie
An artificial rutile and ilmenite technology, applied in the direction of titanium dioxide, titanium oxide/hydroxide, etc., can solve the problems of unsuitable boiling chlorinated raw materials, low grade of artificial rutile, low softening point at high temperature, etc., and achieve easy continuous production , easy equipment material, high concentration effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] A method of the present invention for producing artificial rutile from residual slope ilmenite, which uses 400 g of Yunnan residual slope ilmenite as a raw material (see Table 1 for chemical composition and Table 2 for particle size composition) , Including the following steps:
[0024] (1) Reduction pretreatment: First put ilmenite in a rotary kiln, use coal as a reducing agent, and reduce treatment for 30 minutes at a temperature of 850°C;
[0025] (2) Oxidation pretreatment: The output after the above reduction pretreatment is transferred to the muffle furnace for oxidation treatment. The oxidant used is oxygen. The temperature during the oxidation treatment is controlled at 800-850℃. After 210min of oxidation treatment, the mineral surface has The rutile crystallites and the outer shell of the iron-rich layer are formed; the calcined material to be oxidized is cooled to 90°C to complete the oxidation process;
[0026] (3) Fluidized acid leaching: send th...
Example Embodiment
[0033] Example 2
[0034] A method of the present invention for producing artificial rutile from residual slope ilmenite, the method uses 400g Guangxi residual slope ilmenite as raw material (the chemical composition is shown in Table 3 below, and the particle size composition is shown in Table 4 below) , Including the following steps:
[0035] (1) Reduction pretreatment: First put ilmenite in a rotary kiln, use coal as a reducing agent, and pre-reduction treatment for 15 minutes at a temperature of 900°C;
[0036] (2) Oxidation pretreatment: the output after the above reduction pretreatment is transferred to the muffle furnace for oxidation treatment, the oxidant used is oxygen, and the temperature during the oxidation treatment is controlled at 800°C (parameters have been changed to distinguish it from the original Patent), after 25 minutes of oxidation treatment, rutile crystals and iron-rich shells are formed on the mineral surface; the roasted material to be oxidized is cooled ...
Example Embodiment
[0044] Example 3
[0045] A method of the present invention for producing artificial rutile from residual slope-type ilmenite, which uses 400 grams of Guangxi altered ilmenite as raw material (see Table 5 for chemical composition and Table 6 for particle size composition), It includes the following steps:
[0046] (1) Reduction pretreatment: First put the ilmenite in a rotary kiln, use coal as the reducing agent, and pre-reduction treatment for 215 minutes at a temperature of 850°C;
[0047] (2) Oxidation pretreatment: transfer the above-mentioned reduced discharge to the muffle furnace for oxidation treatment. The oxidant used is oxygen. The temperature during the oxidation treatment is controlled at 800℃. After the oxidation treatment for 10 minutes, there are rutile crystals and crystals on the mineral surface. The iron-rich shell is formed; the roasted material to be oxidized is cooled to 90°C to complete the oxidation process;
[0048] (3) Fluidized acid leaching: the above-ment...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap