Sheet with wood-like texture

A board and texture technology, applied in clay preparation device, mixed operation control device, mixed operation control, etc., can solve the problems of non-fireproof, non-abrasive, perishable, etc.

Inactive Publication Date: 2010-12-08
袁建华
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As a natural resource, wood is the most used substance in daily life by humans. At present, due to the use of a large amount of wood, the forest area has decreased rapidly, making wood increasingly expensive. However, due to the characteristics of wood materials and the long-loved Texture, it is difficult to replace it with other materials, so the demand for wood has not decreased so far
[0003] The disadvantages of wooden boards are that they are not wear-resistant, not fireproof, perishable, easy to be eaten by insects, and expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A board with imitation wood texture is prepared through the following steps: (1) Making a mold: a piece of natural wood can be repaired into a board with a length of 2000 mm, a width of 1000 mm and a height of 5 mm, and the board is processed so that the wood grain of the board is convex. For the surface of the board, put the processed board on the table, cast a square frame with steel along the board, which is 50mm wider than the surrounding of the board and 5mm higher than the upper surface, pour the special mold glue into the frame, and after 8 to 12 hours The mold glue is formed, and the wooden board is taken out so that the inner bottom surface of the mold has imitation wood grain dents; (2) the mixture of 58% cement, 36% sand, 6% synthetic titanium oxide and appropriate amount of water is evenly brushed on the protruding part of the mold Form the texture layer; (3) uniformly spray the mixed material of cement 55%, sand 37%, synthetic titanium oxide 8% and an approp...

Embodiment 2

[0012] A board with imitation wood texture is prepared through the following steps: (1) the method for preparing the mold is the same as in Example 1, and the previous mold can also be reused without preparing the mold; (2) 65% cement, 26% sand, synthetic oxidation The mixture of titanium 9% and appropriate amount of water is evenly brushed onto the protruding part of the mold to form a texture layer; (3) the mixture of cement 62%, sand 26%, synthetic titanium oxide 12% and appropriate amount of water is evenly sprayed on the inner bottom surface of the mold Form the first base material layer of the plate, and the texture layer has color difference with the first base material layer; (4) immediately add 45% of cement, 42% of sand, 5% of glass fiber material, 8% of synthetic titanium oxide and an appropriate amount of water The mixed material is evenly filled into the mold to form the second substrate layer; (5) The operation method of sheet forming is the same as that in Exampl...

Embodiment 3

[0014] A board with imitation wood texture is prepared through the following steps: (1) the method for preparing the mold is the same as in Example 1, and the previous mold can also be reused without preparing the mold; (2) 63% of cement, 30% of sand, synthetic oxidation The mixture of titanium 7% and appropriate amount of water is evenly brushed onto the protruding part of the mold to form a texture layer; (3) the mixture of cement 60%, sand 29%, synthetic titanium oxide 11% and appropriate amount of water is evenly sprayed on the inner bottom surface of the mold Form the first base material layer of the plate, and the texture layer has color difference with the first base material layer; (4) immediately mix 44% cement, 45% sand, 3% glass fiber material, 8% synthetic titanium oxide and an appropriate amount of water The mixed material is evenly filled into the mold to form the second substrate layer; (5) The operation method of sheet forming is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sheet with a wood-like texture, which is prepared by the following steps of: (1) manufacturing a module and making a wood-like dent part on the inner bottom surface of the mould; (2) uniformly brushing a mixed material of 58-65 percent of cement, 26-36 percent of sand, 6-9 percent of compound titanium oxide and proper quantity of water onto a protruding part of the mould to form a texture layer; (3) uniformly brushing a mixed material of 55-62 percent of cement, 26-37 percent of sand, 8-12 percent of compound titanium oxide and proper quantity of water onto the inner bottom surface of the mould to form a first substrate layer of the sheet, wherein the texture layer and the first substrate layer have color difference; (4) then uniformly filling 42-45 percent of cement, 42-47 percent of sand, 3-5 percent of glass fiber materials, 8-10 percent of compound titanium oxide and proper quantity of water into the mould to form a second substrate layer; and (5) condensing and forming the materials, and binding the texture layer, the first substrate layer and the second substrate layer to form the sheet finished product of the invention.

Description

technical field [0001] The invention relates to a board in the field of building decoration and a preparation method thereof, in particular to a wood-like texture board that can be used as an indoor and outdoor decorative wall board and a ceiling decorative board. Background technique [0002] As a natural resource, wood is the most used substance in daily life by humans. At present, due to the use of a large amount of wood, the forest area has decreased rapidly, making wood increasingly expensive. However, due to the characteristics of wood materials and the long-loved Texture, it is difficult to replace it with other materials, so the demand for wood has not decreased so far. [0003] The disadvantages of wooden boards are that they are not wear-resistant, not fireproof, perishable, easy to be eaten by insects, and expensive. Contents of the invention [0004] The purpose of the present invention is to solve the problems in the prior art and provide a wear-resistant, co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F13/08B28B1/16B28C7/04
Inventor 袁建华
Owner 袁建华