Luminous pill for ceramic metal halogen lamp
A technology of ceramic metal halide lamps and luminescent pills, which is applied in the field of light sources, can solve problems such as short service life, low luminous efficiency, and large color drift, and achieve long service life, high luminous efficiency, and good color rendering.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] A luminescent pellet for use in ceramic metal halide lamps, consisting of iodides of dysprosium, holmium, thulium, sodium, thallium, and thorium. The weight ratio of dysprosium iodide, holmium iodide, thulium iodide, sodium iodide, thallium iodide and thorium iodide in the iodide forming the luminescent pill is: 16:20:15:21:20:4. The above-mentioned high-purity metal halides are mixed in a determined ratio and placed in a specific quartz container for pre-vacuum treatment (heating to 100-150°C), and then slowly heated until the mixture melts. Under high temperature conditions, rare earth halides, thorium iodide and sodium iodide form complexes with lower melting points. After stirring for a period of time, the metal halide-complex eutectic with uniform chemical composition is ejected from the nozzle, and the molten beads are rapidly cooled and solidified into balls during the mass transfer process with high-purity inert gas and collected in the product bottle . After ...
Embodiment 2
[0028] The preparation method is the same as in Example 1.
[0029] A luminescent pellet for use in ceramic metal halide lamps, consisting of iodides of dysprosium, holmium, thulium, sodium, thallium, and thorium. The weight ratio of dysprosium iodide, holmium iodide, thulium iodide, sodium iodide, thallium iodide and thorium iodide in the iodide forming the luminescent pill is: 19:16:19:28:19:4. The luminescent pill has a diameter of 0.6 mm and a grain weight of 0.7 mg. The luminous efficiency of the ceramic metal halide lamp produced by the pill is 100lm / w, the color rendering index is 93, the correlated color temperature is 4200K, the service life is 10000h, and the color drift is ±190k.
Embodiment 3
[0031] The preparation method is the same as in Example 1.
[0032] A luminescent pellet for use in ceramic metal halide lamps, consisting of iodides of dysprosium, holmium, thulium, sodium, thallium, and thorium. The weight ratio of dysprosium iodide, holmium iodide, thulium iodide, sodium iodide, thallium iodide and thorium iodide in the iodide forming the luminescent pill is: 20:18:20:27:13:4. The luminescent pill has a diameter of 0.8 mm and a grain weight of 1.1 mg. The luminous efficiency of the ceramic metal halide lamp produced by the pill is 100lm / w, the color rendering index is 93, the correlated color temperature is 4200K, the service life is 10000h, and the color drift is ±200k.
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
weight | aaaaa | aaaaa |
luminous efficiency | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap