Manufacturing method and production process formula of stone-like and wood-like concrete rails

A manufacturing method and technology of production process, applied in the field of manufacturing imitation stone concrete railings, can solve the problems of waste of concrete affecting the production quality of railing products, service life of only one year, inconvenient handling and operation, etc., and achieve low production cost and high quality. Hard, simple and reasonable structure

Inactive Publication Date: 2011-05-25
SHANGHAI SHANGTENG INDAL DEV
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the mold is heavy and inconvenient to carry and operate
And because the mold shell of FRP is made by hand, the dimensional accuracy is low, the interchangeability is poor, and the surface of the mold shell is hard and thin, and it is easy to warp and deform. Production quality and waste of concrete; in addition, molds are prone to aging and have a service life of only one year

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The following are specific examples of the present invention to further describe the technical solution of the present invention, but the present invention is not limited to the following examples.

[0029] The manufacture method of imitation stone and imitation wood concrete railing of the present invention, its steps:

[0030] 1) Mold preparation: clean the inner surface of the imitation stone mold or imitation wood mold, and apply a release agent on the inner wall of the mold. The release agent is LEYCO-SLICK with a concentration of 5%.

[0031] 2) Mixing material preparation: weigh the mixing material according to the proportion, the mixing material ratio is: take a bag of cement 50 kg as an example, cement: 50 kg, yellow sand: 94.5 kg, gravel: 202 kg, water: 26.9 kg . The cement adopts 425 low alkalinity sulfoaluminate rapid hardening cement.

[0032] 3) Stirring: Since the original material in the present invention has low-alkalinity sulphoaluminate cement, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to rails, in particular to a manufacturing method of stone-like concrete rails suitable for decoration engineering of water conservancy watercourses, municipal bridges, landscape boardwalks, reservoir enclosures and the like. The method comprises the following steps: 1) preparing a mould; 2) preparing stirred materials; 3) stirring the stirred materials; 4) stirring the stirred materials thrown each time for N minutes; 5) moulding the mixture; 6) vibrating the mixture; 7) airing the mixture; 8) removing the mould; 9) curing the rails; and 10) treating the surfaces of the stone-like and wood-like concrete rails. The mould and the manufacturing method have the following advantages: simple production steps, energy saving, environmental protection, low cost, simple and reasonable structure, convenience in use, perfect and vivid effect, high strength, water resistance, weather resistance and the like.

Description

technical field [0001] The invention relates to a railing, in particular to a method for manufacturing a stone-like concrete railing suitable for decoration projects such as water conservancy channels, municipal bridges, landscape plank roads, and reservoir enclosures. Background technique [0002] Existing railings are all made of metal or wood. The former has cumbersome molding, high labor intensity, low work efficiency, high energy consumption and high cost. The latter must be coated with protective paint, which is not only complicated and cumbersome, time-consuming, but also easy to fade and difficult to shape. The labor intensity is high and the cost is high; moreover, it consumes a large amount of wood, which damages the environment and affects the ecological balance. [0003] Wrought iron railings are easy to steal and rust, and they need to be painted and maintained every year, which greatly wastes manpower, material resources and financial resources. Stainless st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B28B1/14B28B1/04B28B11/24E01D19/10E04H17/14
Inventor 季军
Owner SHANGHAI SHANGTENG INDAL DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products