Method for preparing low-SiO2 high-performance sinter ore

A high-performance technology for sintered ore, applied in the field of iron ore powder sintering, can solve the problems of deterioration of low-temperature reduction pulverization index and low sintering ore strength, and achieve the effect of ensuring strength and low-temperature pulverization performance

Active Publication Date: 2011-07-20
SHOUGANG CORPORATION
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The object of the present invention is to provide a low SiO 2 High-performance sinter preparation method overcomes the previous reduc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing low-SiO2 high-performance sinter ore
  • Method for preparing low-SiO2 high-performance sinter ore
  • Method for preparing low-SiO2 high-performance sinter ore

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Below in conjunction with accompanying drawing and specific embodiment the present invention is described in further detail:

[0023] As shown in the figure, the sinter preparation process of the present invention is roughly divided into: raw material allocation - mixing - granulation - distribution - ignition - sintering - crushing - cooling - sinter index detection - metallurgical performance detection and other settlements, its specific operation steps as follows:

[0024] 1) Raw materials: 75-85% of iron-containing raw materials, 3.5-4.5% of quicklime, 3.5-5.0% of dolomite, 2.0-3.5% of limestone, and 4.5-6.0% of coke powder. ;

[0025] 2) Mixing: transport the selected raw material components into a primary cylinder mixer, add an appropriate amount of water to wet the material, control the water distribution of the raw material between 7±0.3%, and make the raw material mix evenly;

[0026] 3) Granulation: Transport the uniformly mixed raw materials to the secondar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a low-SiO2 high-performance sinter ore, and belongs to the technical field of sintering of iron ore powder. The method comprises the following steps of: proportioning; mixing; granulating; dispensing; igniting; sintering; crushing; cooling; detecting indexes of the sinter ore; detecting a reduction property; and detecting low-temperature reduction degradation performance. The sinter core comprises the following raw materials in percentage by weight: 75 to 85 percent of iron-containing raw material, 3.5 to 4.5 percent of quick lime, 3.5 to 5.0 percent of dolomite, 2.0 to 3.5 percent of limestone and 5.0 to 6.0 percent of coke powder; and alkalinity CaO/SiO2 of the sinter core is equal to 1.8 to 2.0, TFe content is between 55 and 60 percent, SiO2 content is between 4.2 and 4.5 percent, MgO content is between 1.9 and 2.3 percent, and FeO content is between 8 and 10 percent, wherein the FeO content in the sinter core is realized by a method for increasing the proportion of the coke powder, and the proportion of the coke powder is increased from 3.0-4.0 percent to 5.0-6.0 percent; and finally, a drum index of the sinter core is increased from 82 percent to 83.6 percent, a low-temperature reduction degradation index RDI+3.15 is increased from 39 percent to 51 percent, and a reduction index is increased from 79 percent to 85 percent under conditions of low SiO2 and high FeO.

Description

technical field [0001] The invention belongs to the technical field of iron ore powder sintering, in particular to a low-SiO 2 The high-performance sinter preparation method is to use the existing raw materials and equipment to reasonably control the FeO of the sinter, to ensure the strength of the sinter, and to improve the reducibility and low-temperature pulverization performance of the sinter. Background technique [0002] The performance of sinter has an important influence on the various technical and economic indicators of the blast furnace; the principle of fine material requires that the grade of sinter be increased as much as possible (and then the grade of entering the furnace be increased). Reduce SiO of sinter 2 content, not only can improve the grade of sintered ore, but also can reduce the amount of blast furnace slag, improve the air permeability of blast furnace, and reduce the coke ratio. Therefore, more and more researchers pay full attention and Researc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/16
Inventor 裴元东赵志星马泽军赵勇潘文秦岳义
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap