High-gloss paint for vacuum aluminized paper and preparation method and application thereof

A vacuum aluminized paper, high-gloss technology, applied in the direction of paper coating, coating, papermaking, etc., can solve the problems of poor storage stability, environmental pollution, strong odor, etc., achieve improved wear resistance and storage stability, and improve durability Abrasion resistance, effect of improving cohesive strength

Active Publication Date: 2012-12-19
SHANGHAI DONGSHENG NEW MATERIALS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the high-gloss coatings for vacuum aluminum-coated paper are solvent-based, alcohol-soluble, and emulsion-based coatings. Among them, solvent-based and alcohol-soluble coatings contain a large amount of organic solvents, which have a strong smell and are easy to pollute the environment.
[0004] Chinese patent (CN101250834A) discloses a kind of surface coating coating for vacuum metallized paper treatment, by adding acrylic resin, acrylate resin, neutralizing agent, leveling agent and wear-resistant agent etc. to prepare the vacuum metalized paper surface coating coating It has excellent transparency and abrasion resistance, but it needs to add anti-abrasion agent, and its storage stability is slightly poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-gloss paint for vacuum aluminized paper and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] With 0.5 gram of hydroxyethyl acrylate (acid value 5mgKOH / g, hydroxyl value 40mgKOH / g), 2 grams of polyvinyl alcohol (weight-average molecular weight 2000, degree of alcoholysis is 50%), 5 grams of acrylic resin (acid value 150mgKOH / g, the molecular weight is 1000), 0.5 grams of diethanolamine and 75 grams of water were mixed, and the temperature was raised to 80°C to obtain solution A. Then solution A, 100 grams of acrylate resin (glass transition temperature Tg is -10 ° C), 0.1 grams of polydimethylsiloxane, 0.2 grams of polyester modified silicone and 425 grams of water were mixed and stirred for 30 minutes to obtain High-gloss coating for vacuum aluminized paper treatment, pH value is 6.5, weight solid content is 15.0%.

Embodiment 2

[0030] With 1.5 grams of diethylene glycol monoacrylate (acid value 8mgKOH / g, hydroxyl value 50mgKOH / g), 5 grams of polyvinyl alcohol (weight-average molecular weight 4000, degree of alcoholysis is 70%), 15 grams of acrylic resin ( The acid value is 280mgKOH / g, the molecular weight is 3000), 7 grams of triethylamine and 100 grams of water are mixed, and the temperature is raised to 55° C. to obtain solution A. Then solution A, 100 grams of acrylate resin (glass transition temperature Tg is 0 ° C), 0.5 grams of tributyl phosphate, 0.5 grams of silicone-modified polyacrylate and 300 grams of water were mixed and stirred for 30 minutes to obtain vacuum aluminized High gloss coating for paper treatment, pH 5.0, 22.8% solids by weight.

Embodiment 3

[0032] With 2 grams of hydroxypropyl acrylate (acid value 12mgKOH / g, hydroxyl value 60mgKOH / g), 10 grams of polyvinyl alcohol (weight average molecular weight 10000, degree of alcoholysis is 80%), 35 grams of acrylic resin (acid value 400mgKOH / g, the molecular weight is 5000), 15 grams of diethanolamine and 138 grams of water were mixed, and the temperature was raised to 80°C to obtain solution A. Then solution A, 100 grams of acrylate resin (glass transition temperature Tg is 30 ° C), 1.0 grams of lauryl phenylacetate, 0.8 grams of polyester-modified silicone and 92 grams of water were mixed and stirred for 30 minutes to obtain a vacuum aluminum coating High gloss coating for paper treatment, pH 8.0, 40.0% solids by weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to view more

Abstract

The invention provides high-gloss paint for vacuum aluminized paper and a preparation method and application thereof. The high-gloss paint comprises the following components in parts by weight: 0.5-2.0 parts of hydroxyl acrylate resin, 2-10 parts of polyvinyl alcohol, 5-35 parts of acrylic resin, 0.5-15 parts of neutralizer, 100 parts of acrylate resin, 0.1-1.0 part of defoaming agent, 0.2-0.8 part of flatting agent and 500-1000 parts of water. As for the prepared high-gloss paint for treatment of vacuum aluminized paper, the solid weight content is 15-40%, and the pH value is 5-8. Besides, the high-gloss paint can effectively overcome the disadvantages of the existing process, so that the gloss, abrasive resistance and storage stability of the paint are greatly improved.

Description

technical field [0001] The invention relates to a preparation method and application of a high-gloss coating for vacuum aluminized paper. Background technique [0002] Vacuum aluminum-coated paper is mainly composed of base paper, aluminum layer and coating. It has good gloss and smoothness, good flexibility, high fastness of the aluminum sprayed layer, beautiful and environmentally friendly, and has good printing performance and machining performance. The surface strength of aluminized paper is high, it can adapt to the speed of high-speed printing machines, and can also bear the tension caused by the increase in ink viscosity, which has good adaptability to improve production efficiency and stabilize printing quality. The surface tension of aluminized paper is conducive to the transfer of ink during printing, and the printing ink film is flat, smooth, and the graphics and texts are clear and complete. Therefore, it can be widely used in the exquisite packaging of tobacco,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21H19/22D21H19/20D21H19/08
Inventor 施晓旦王养臣周海波
Owner SHANGHAI DONGSHENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap