A kind of propylene and phenol alkylation reaction catalyst and preparation method thereof
A technology of phenol alkylation and catalyst, which is applied in the field of propylene and phenol alkylation reaction catalyst and its preparation, and can solve the problems of low efficiency, waste of resources, inability to reuse, etc.
Active Publication Date: 2016-08-17
宣城市聚源精细化工有限公司
View PDF3 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] The catalyst used in the existing industrial technology for the alkylation reaction of propylene and phenol is p-hydroxybenzenesulfonic acid, and its reaction time is generally as long as 10-12 hours. The reaction time is relatively long, and the conversion rate is only about 90%. , and p-hydroxybenzenesulfonic acid cannot be reused as a catalyst, and the use efficiency is very low, which causes a certain waste of resources. Therefore, we began to look for a high-efficiency catalyst that can be reused
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment
[0013] Example: 450 kg of propylene and 1000 kg of phenol were put into a reactor, and 50 kg of the catalyst of the present invention was added at the same time, at a temperature of 105°C under normal pressure. After 7 hours of reaction, the conversion rate of the reactants was measured to be 98.2%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides a catalyst for the alkylation reaction of propylene and phenol, which comprises the following weight percentages of raw materials: 30-40% of diatomite, 15-25% of epoxy resin, and 40-50% of p-hydroxybenzenesulfonic acid. After the formula raw materials are mixed, dried, processed into granules, and dried again to obtain the finished product. The catalyst of the invention is applied to the alkylation reaction of propylene and phenol, which can shorten the alkylation reaction time, increase the conversion rate and reduce the production cost.
Description
technical field [0001] The invention relates to the field of alkylation reaction of organic matter, in particular to a catalyst for alkylation reaction of propylene and phenol and a preparation method thereof. Background technique [0002] The catalyst used in the existing industrial technology for the alkylation reaction of propylene and phenol is p-hydroxybenzenesulfonic acid, and its reaction time is generally as long as 10-12 hours. The reaction time is relatively long, and the conversion rate is only about 90%. , and p-hydroxybenzenesulfonic acid cannot be reused as a catalyst, and the use efficiency is very low, which causes a certain waste of resources. Therefore, we began to look for a high-efficiency catalyst that can be reused. Contents of the invention [0003] The invention provides a catalyst for the alkylation reaction of propylene and phenol and a preparation method thereof. The use of the catalyst improves the speed of the alkylation reaction of propylene ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/06C07C39/06C07C37/14
Inventor 程聚光
Owner 宣城市聚源精细化工有限公司