Preparation method of printed synthetic leather

A synthetic leather and printing technology, applied in the directions of dyeing, fabric elongation, heating/cooling fabric, etc., can solve the problems of low production efficiency, high cost, poor color fastness of synthetic leather printing, etc. Guaranteed color fastness and improved accuracy

Active Publication Date: 2013-06-05
QUANZHOU WANHUA SEWANG MICRO FIBER CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main purpose of the present invention is to overcome the shortcomings of the prior art, to provide a preparation method of printed synthetic leather, which can overcome the shortcomings of synthetic leather printing color fastness, low production efficiency, high cost, etc., the surface of the printed synthetic leather produced Wide variety of colors and patterns, suitable for large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of preparation method of printed synthetic leather of the present invention is realized by following steps:

[0022] 1. The thickness is 1.3mm and the weight is 230g / m 2 , a conventional fiber non-woven fabric with a width of 152cm and a weight ratio of nylon / polyester=20 / 80, the non-woven fabric is elongated by 5% in the warp direction through directional stretching equipment, and is shaped at a high temperature at 150°C to obtain a thickness of 1.0mm , A shaped non-woven fabric with a width of 148cm;

[0023] 2. The shaped non-woven fabric is wet-processed, the directional elongation is 4%, and it is shaped at a high temperature under the condition of 150°C to obtain the shaped base fabric;

[0024] 3. Dry the shaped base cloth on the dry line to obtain the initial product;

[0025] 4, prepare three kinds of color printing inks of ether ester copolymerized PU resin: colorant: solvent=15: 25: 135, carry out 3-color overprint printing with above-mentioned ink o...

Embodiment 2

[0027] A kind of preparation method of printed synthetic leather of the present invention is realized by following steps:

[0028] 1. The thickness is 1.4mm and the weight is 230g / m 2 , 150cm in width, 100% polyester conventional fiber non-woven fabric, through directional stretching equipment, the non-woven fabric is elongated by 3% in the warp direction, and set at a high temperature at 150°C to obtain a shape with a thickness of 1.0mm and a width of 148cm non-woven fabric;

[0029] 2. The shaped non-woven fabric is wet-processed, and the directional elongation is 3%, and it is shaped at a high temperature under the condition of 150°C to obtain a shaped base fabric;

[0030] 3. Dry the shaped base cloth on the dry line to obtain the initial product;

[0031] 4. Prepare polyester type PU resin: color paste: two color printing inks of solvent = 15: 20: 235, carry out two-color overprint printing with the above-mentioned ink on the initial product on the gravure overprint pri...

Embodiment 3

[0033] A kind of preparation method of printed synthetic leather of the present invention is realized by following steps:

[0034] 1. The thickness is 2.6mm and the weight is 500g / m 2 , width 155cm, nylon / polyethylene=50 / 50 blended superfine fiber non-woven fabric, the non-woven fabric is elongated by 3.5% in the warp direction through directional stretching equipment, and is shaped at a high temperature under 150°C to obtain a thickness of 1.8 mm, width 150cm stereotyped non-woven fabric;

[0035] 2. The shaped non-woven fabric is wet-processed, and the directional elongation is 5%, and it is shaped at a high temperature under the condition of 150° C. to obtain a shaped superfine fiber base cloth;

[0036] 3. Dry the shaped base cloth on the dry line to obtain the initial product;

[0037] 4. Prepare four kinds of color printing inks of polyether type PU resin: color paste: solvent = 15: 25: 85, carry out 4-color overprint printing with the above-mentioned ink on the initia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of printed synthetic leather. The printed synthetic leather is prepared by a non-woven fabric warp direction directional elongation and high-temperature sizing step, a wet process warp direction directional elongation and high-temperature sizing step, a dry method face making step and a plate printing step using at least two colors of printing ink. Compared with the prior art, the defects such as the poor printing color fastness, low production efficiency, high cost and the like of the synthetic leather can be overcome; and the prepared printed synthetic leather has rich apparent flower color and patterns, and can be produced in a large scale.

Description

technical field [0001] The invention relates to a printing method for synthetic leather. Background technique [0002] Usually, the process of transferring the graphic information on the original manuscript to the substrate, and making the dye or pigment form a pattern on the substrate is printing. Printing is partial coloring, which requires a certain color fastness. The printing of two or more colors on the substrate is called register printing. After register printing, regular and multi-color patterns are formed on the substrate. [0003] Process printing has become very common in paper printing such as newspapers and advertisements, clothing fabric printing and plastic packaging materials. The printing methods can be divided into gravure printing, letterpress printing, screen printing, lithographic printing, flexo Thermal transfer printing, etc.; monochrome printing is also widely used in synthetic leather, and gravure and letterpress printing are mostly used. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P5/00D06P3/24D06P3/52D06P3/82D06P1/52D04H3/005D04H1/4382D06C3/00D06C7/02
Inventor 蔡鲁江颜俊李革宋志刚杨新平
Owner QUANZHOU WANHUA SEWANG MICRO FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com