High-temperature solar selective absorption coating and preparation method thereof

A solar energy absorption and selective technology, applied in solar thermal power generation, coatings, solar thermal devices, etc., can solve the problems of rising emission ratio of coatings, unsuitable for use in high temperature conditions, etc., and achieve dense coatings and good infrared reflection. Ability and emission ratio performance, excellent effect of anti-oxidation performance

Inactive Publication Date: 2012-02-15
SHANDONG LINUO NEW MATERIAL
View PDF11 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the temperature rises, the emissivity ratio of the coating also rises sharply, which is not suitable for use at high temperatures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature solar selective absorption coating and preparation method thereof
  • High-temperature solar selective absorption coating and preparation method thereof
  • High-temperature solar selective absorption coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] use figure 2 The magnetron sputtering coating machine sputters Cu / NiCrAlY-AlN / SiAl-O high temperature solar selective absorption coating, target 5 is Cu target, target 6 is NiCrAlY alloy target, target 7 is pure Al target, target 8 is SiAl Target (Al content is 10% by weight), the preparation method is as follows:

[0039] Deposit metal bottom layer: After the vacuum degree of the vacuum chamber reaches the requirement, fill it with argon gas of 40 sccm to keep the pressure of the vacuum chamber at 0.4Pa, open the Cu target, and the sputtering power is 10kW, and stop when the thickness reaches 300nm;

[0040] Absorbing layer deposition: fill 40sccm argon and 48sccm nitrogen through the intake pipe, turn on the NiCrAlY target and the Al target, the NiCrAlY target power is 4kW, the Al target power is 6kW, and stop when the thickness reaches 74nm, as the first absorption layer; The NiCrAlY target power is reduced to 2.5kW, the nitrogen gas is reduced to 42sccm, and the d...

Embodiment 2

[0046] use figure 2 The magnetron sputtering coating machine sputters Cu / NiCrAlY-AlN / AlN high-temperature solar energy selective absorption coating, the target 5 is a Cu target, the target 6 is a NiCrAlY alloy target, and the target 7 is a pure Al target. The preparation method is as follows:

[0047] Deposit the metal bottom layer: After the vacuum degree of the vacuum chamber reaches the requirement, fill it with 40 sccm of argon gas to keep the pressure of the vacuum chamber at 0.4Pa, open the Cu target, and the sputtering power is 10kW, and stop when the thickness reaches 400nm;

[0048] Absorbing layer deposition: fill 40sccm argon and 47sccm nitrogen through the intake pipe, turn on the NiCrAlY target and the Al target, the NiCrAlY target power is 3.8kW, the Al target power is 6kW, and the deposition stops when the thickness is 52nm, as the first absorption layer; Reduce the power of the NiCrAlY target to 2.8kW, reduce the nitrogen gas to 44sccm, and stop when the thick...

Embodiment 3

[0053] use figure 2 The magnetron sputtering coater sputters Cu / NiCrAlY-SiAlN / SiAlO high-temperature solar energy selective absorption coating, the target 5 is a Cu target, the target 6 is a NiCrAlY alloy target, and the target 7 is a SiAl target (the Al content is 18% by weight) The preparation method is as follows:

[0054] Deposit metal bottom layer: After the vacuum degree of the vacuum chamber reaches the requirement, fill it with 40sccm of argon gas to keep the pressure of the vacuum chamber at 0.4Pa, turn on the Cu target, and the sputtering power is 10kW, and stop when the thickness reaches 450nm;

[0055] Deposition of the absorbing layer: fill in 40sccm argon and 54sccm nitrogen through the intake pipe, turn on the NiCrAlY target and the SiAl target, the power of the NiCrAlY target is 4.5kW, and the power of the SiAl target is 6kW, and stop when the thickness reaches 90nm, as the first absorbing layer; Reduce the power of the NiCrAlY target to 3kW, reduce the nitro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-temperature solar selective absorption coating, which comprises an infrared highly-reflective bottom layer, an optical selective absorption layer and an antireflection layer in sequence from bottom to top, wherein the infrared highly-reflective bottom layer is a pure metal film; the optical selective absorption layer comprises two layers of NiCrAlY-M metal ceramic films with different NiCrAlY alloy contents, wherein M is AlN or SiAl alloy nitride; and the antireflection layer is a dielectric film. The invention also discloses a preparation method of the high-temperature solar selective absorption coating. The preparation method is easy to adjust and control; and the coating obtained by adopting the preparation method has favorable high-temperature resistanceproperty, infrared ray reflection capability and emission rate property, good spectrum absorption property and strong mechanical property.

Description

technical field [0001] The invention relates to a solar absorbing coating and a preparation method thereof, in particular to a solar selective absorbing coating which can still be used at high temperatures and a preparation method thereof. Background technique [0002] With the development of human science and technology and the improvement of productivity, the problem of energy shortage is gradually exposed. The depletion of traditional energy such as oil and natural gas has restricted the continued development and progress of mankind. Under the new situation of global energy shortage, the development of solar energy is economical and environmentally friendly, and it is a new way to alleviate energy shortage. [0003] The solar selective absorbing coating is the core part of the solar thermal process, by absorbing sunlight and converting it into heat. Excellent solar selective absorbing coatings have a higher absorption ratio α value in the solar spectrum (wavelength 0.3~...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F24J2/48C23C14/35C23C14/14C23C14/06C23C14/08
CPCF24S70/225F24S70/25F24S70/30Y02E10/40
Inventor 李业博刘希杰吴旭林柯伟张化明
Owner SHANDONG LINUO NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap