A composite material and antistatic masterbatch technology, which is applied in chemical instruments and methods, other chemical processes, etc., can solve the problem that the conductivity is lower than that of metal materials, achieve good antistatic effect, improve compatibility, and increase surface activity. Effect
Active Publication Date: 2012-04-04
上海日之升科技有限公司
View PDF2 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
It is suitable for making general mechanical parts, corrosion-resistant parts and automobile and electrical parts. However, PP has good electrical insulat
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-5
[0023] The raw material formulations of the antistatic masterbatch of Examples 1-5 are as follows:
[0024]
[0025] In the above embodiment, the alkali metal salt is M + X - , Where M + Li + , Na + , K + ; X - For Cl - , Br - , I - , CLO 4 - , Preferably LiCLO 4 .
[0026] In the foregoing embodiment, the antioxidant is a 1:1 compound of phenothiazine and phosphite (s9228);
[0027] In the foregoing embodiment, the heat stabilizer is a 2:1:1 compound of organotin heat stabilizer, calcium stearate, and zinc stearate;
[0028] In the foregoing embodiment, the antistatic agent is silica;
[0029] In the above embodiment, the polymer material containing polyether block is a 5:1 compound of polyethylene oxide and polyethylene glycol methacrylic acid copolymer; the molecular weight of the two polymers is preferably 6 Between 160,000.
[0030] Put the above-mentioned components into a high-mixer in proportion to mix for 2-5 minutes, discharge the material, and then extrude and pelletize with ...
Embodiment 5
[0036] Example 5 has the lowest surface resistivity and the highest cost performance.
Embodiment 6
[0051] Weigh the raw materials according to the weight ratio: 1% of the above-mentioned antistatic masterbatch, 98% PP, and 1% of the compatibilizer. Weigh the raw materials according to the weight ratio, put them in a high-mixer and mix for 2-5 minutes, then discharge, Then use a twin-screw extruder to extrude and pelletize, the processing temperature is 190-220℃, and the screw rotation speed is 40 Hz. The surface resistivity of the prepared material is 10 13 Ω.m.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Melt index
aaaaa
aaaaa
Notched impact strength
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a permanent anti-static PP (polypropylene) composite material and a preparation method thereof. The material comprises the following components in percentage by weight: 3 to 8 percent of anti-static master batch, 80 to 95 percent of PP and 1 to 5 percent of compatilizer. The preparation method comprises the following steps of: weighing the raw materials according to weight proportion; placing the raw materials into a high mixing machine to mix the raw materials for 2 to 5 minutes; discharging; and then carrying out extrusion pelletizing by a double-screw extruder, wherein a processing temperature is in the range of 190 to 220 DEG C and screws have revolution of 35 to 40Hz. Compared with the prior art, the permanent anti-static PP composite material has the advantages of sustained anti-static effect, permanent anti-static effect, good anti-static effect, high comprehensive mechanical property, performance close to pure PP, light color, capability of being prepared into various colors, low cost, good heat resistance and the like. The surface resistivity of the permanent anti-static PP composite material can reach 106 to 108 ohm.m.
Description
Technical field [0001] The invention relates to a permanent antistatic masterbatch and a preparation method. The invention also relates to a method for preparing permanent antistatic PP composite material. Background technique [0002] PP is non-toxic, tasteless, low density, low price, and has good electrical properties. Common acid and alkali organic solvents have almost no effect on it. It is suitable for making general mechanical parts, corrosion-resistant parts and automobile and electrical parts. But PP has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω.m, the conductivity is much smaller than that of metal materials. It is easy to accumulate static charge when it comes into contact with other substances or rubs. The negative effects of static electricity accumulation have seriously affected production, life, and work, and sometimes even cause fires and explosions. In some specific working environments in t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more