Gold glaze pigment for glass and method for applying gold glaze on glass wine bottles

A gold and glass technology, applied in the field of glazing of glass products, can solve the problems of glaze color development and poor adsorption, and achieve the effect of improving grade and added value, and the color is noble and elegant

Active Publication Date: 2013-08-07
JIANGSU BAIFU TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of golden glaze pigment for glass and a method for applying golden glaze on glass wine bottles in view of the problems existing in the prior art, which solves the problems of glaze material color development and poor adsorption in the prior art. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Ingredients according to the following ingredients (weight percentage): SiO 2 56.6%, B 2 o 3 16%, ZnO 9.4%, Na 2 O 8.3%, K 2 O 2.2%, sodium fluoride 2.3%, Li 2 O 4%, Al 2 o 3 , 1.2%, take the above-mentioned raw materials, stir and mix after passing through a 40-mesh sieve, and make flux raw meal;

[0041] (2) Put the raw material of the above-mentioned flux in the frit kiln, melt it at a high temperature of 1500 ℃, and the firing period is 20 hours. The particle size is above mesh, and then crushed by airflow for later use;

[0042] (3) Preparation of golden glaze pigments: 10% of bright golden agent and 90% of pulverized flux are used to prepare bright golden glaze pigments for glass, wherein the bright golden agents are NiO and CuO, and the weight percentage of the two is 45% for NiO, CuO55%;

[0043](4) Add varnish and thinner oil to the pigment, the ratio of the three is:

[0044] Pigment: varnish: diluent oil = 1:1:0.3, and it is pressed into ink b...

Embodiment 2

[0047] (1) According to the following ingredients (weight percentage): SiO2 56.6% B2O3 16% ZnO 9.4% Na2O 8.3% K2O 2.2%, lithium fluoride 2.3% Li2O 4% Al2O3 1.2%, weigh the above raw materials, pass through 60 mesh Stir and mix after sieving to make flux raw meal;

[0048] (2) Put the raw material of the above-mentioned flux in the frit kiln, melt it at a high temperature of 1600 ℃, and the firing cycle is 22 hours. The particle size is above mesh, and then crushed by air flow for use;

[0049] (3) Preparation of deep bright golden glaze pigment: 15% of bright golden agent and 85% of pulverized flux are mixed to form dark bright golden glaze pigment for glass, wherein the bright golden agent is CoO and CuO, and the weight percentage of the two is that CoO is 40%, CuO60%;

[0050] (4) Same as embodiment 1;

[0051] (5) Spray the ink on the surface of the glass wine bottle with a glaze sprayer, place it in a gas kiln and fire it under an oxidizing atmosphere at 580°C, and the ...

Embodiment 3

[0053] (1) According to the following ingredients (weight percentage): SiO2 56.6% B2O3 16% ZnO 9.4% Na2O 8.3% K2O 2.2%, potassium fluoride 2.3% Li2O 4% Al2O3 1.2%, weigh the above raw materials, pass through 60 mesh Stir and mix after sieving to make flux raw meal;

[0054] (2) Put the raw material of the above-mentioned flux in the frit kiln, melt it at a high temperature of 1550 ℃, and the firing cycle is 21 hours. The particle size is above mesh, and then crushed by air flow for use;

[0055] (3) Preparation of matte golden glaze pigment: 20% of bright golden agent and 80% of pulverized flux are mixed to form matt golden glaze pigment for glass, wherein the bright golden agent is MnO and CuO, and the weight percentage of the two is MnO is 40%, CuO60%;

[0056] (4) Same as embodiment 1;

[0057] (5) Spray the ink on the surface of the glass wine bottle with a glaze sprayer, place it in a gas kiln and fire it under an oxidizing atmosphere at 560°C, and the firing time is c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a gold glaze pigment for glass and a method for applying gold glaze on glass wine bottles. The method includes: firstly, preparing a solvent and adding gold agents of different proportions into the solvent to prepare different-color gold glaze pigments for glass; secondly, mixing the pigments, varnish and fluxing oil proportionally to form oil ink, spraying the oil ink onto surfaces of the glass wine bottles, and firing to obtain the glass wine bottles having effects of ceramic wine bottles. Components of the solvent mainly include SiO2, B2O3, ZnO, Na2O, K2O, Li2O, Al2O3 and fluoride, wherein the fluoride is one of sodium fluoride, lithium fluoride or potassium fluoride or a compound of two of sodium fluoride, lithium fluoride or potassium fluoride. The gold glazepigment for glass and the method for applying gold glaze on the glass wine bottles have the advantages that problems of poor color rendering and poor color adsorption of glaze in the prior art are solved, effect of the glass wine bottles applied with gold glaze is similar to that of ceramic wine bottles, color and luster of the glass wine bottles are noble and elegant, grade and additional value of the glass wine bottles are increased, and accordingly the glass wine bottles are popular with the market deeply.

Description

technical field [0001] The invention relates to the technical field of glazing for glass products, in particular to a golden glaze for glass and a method for applying gold glaze based on a glass wine bottle. Background technique [0002] Glass products are generally decorated with decals and direct printing. Since glass has no water absorption, it is not as easy to glaze as ceramics, so the decoration efficiency is not as rich as ceramics. In recent years, with the improvement of people's living standards, the demand for commodities Packaging requirements are getting higher and higher, especially the decoration of ceramic wine bottles, which have collection value, so gold glaze is applied on glass wine bottles to make its effect similar to that of ceramic wine bottles, and its market usage is quite huge. [0003] In the prior art, some progress has been made in printing patterns on the glass surface with glass as the substrate, but how to solve the problem of adsorption betw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86C03C8/00
Inventor 周孟大范盘华李传猛吴群芳
Owner JIANGSU BAIFU TECH CO LTD