Formula of cement slurry with high concretion rate

A cement slurry and high calculus technology, which is applied in the formulation field of cement slurry with high calculus rate, can solve the problems of low cement slurry solidity rate and low solidification strength, and achieve the effect of improving the solidification strength and grouting reinforcement effect

Inactive Publication Date: 2012-07-11
SHANXI LUAN ENVIRONMENTAL ENERGY DEV +1
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The technical problem to be solved by the present invention is that the cement slurry in the prior art has low solidity rate and low solidification strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The formula of cement slurry with high calculus rate is composed of cement, water, flaky ultrafine light-burned kaolin, sodium polyacrylate or naphthalenesulfonic acid formaldehyde condensation product water reducer, and low-viscosity methyl carboxyl cellulose, of which: the quality of cement and water The ratio is 1:1; the amount of flaky ultrafine lightly burned kaolin is 10% of the cement mass; the amount of sodium polyacrylate or naphthalenesulfonic acid formaldehyde condensation product water reducer is 0.3% of the cement mass; low viscosity methyl carboxy cellulose The dosage is 0.3% of the cement mass.

Embodiment 2

[0026] The formula of cement slurry with high calculus rate is composed of cement, water, flaky ultrafine light-burned kaolin, sodium polyacrylate or naphthalenesulfonic acid formaldehyde condensation product water reducer, and low-viscosity methyl carboxyl cellulose, of which: the quality of cement and water The ratio is 1:0.7; the amount of flaky ultrafine lightly burned kaolin is 15% of the cement mass; the amount of sodium polyacrylate or naphthalenesulfonic acid formaldehyde condensation product water reducer is 0.4% of the cement mass; low viscosity methyl carboxy cellulose The dosage is 0.4% of the cement mass.

Embodiment 3

[0028] The formula of cement slurry with high calculus rate is composed of cement, water, flaky ultrafine light-burned kaolin, sodium polyacrylate or naphthalenesulfonic acid formaldehyde condensation product water reducer, and low-viscosity methyl carboxyl cellulose, of which: the quality of cement and water The ratio is 1:0.65; the amount of flaky ultrafine light-burned kaolin is 20% of the cement mass; the amount of sodium polyacrylate or naphthalenesulfonic acid formaldehyde condensation product water reducer is 0.5% of the cement mass; low-viscosity carboxylated cellulose The dosage is 0.5% of the cement mass.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
strengthaaaaaaaaaa
stone rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula of cement slurry with high concretion rate. The formula of the cement slurry with the high concretion rate comprises cement, water, flaky superfine light-burned kaolin, sodium polyacrylate or a naphthalene sulfonic acid-formaldehyde condensate water-reducing agent and low-viscosity carboxymethyl cellulose. The concretion rate of the cement slurry prepared by the technical scheme provided by the invention can achieve 93-95%, and under the same conditions, the concretion rate can be improved by 23-25% in comparison with the cement slurry which is used currently, and the improvement rate is about 33-36%. The cement slurry can significantly improve the effects of grouting and water blocking.

Description

technical field [0001] The invention relates to a formula of cement slurry with high calculus rate. Background technique [0002] Cement slurry is the most important grouting material. It is mainly used for the reinforcement of roadways, foundations, culverts, dams and other projects, and is also used for grouting water blocking, grouting fire extinguishing and other fields. [0003] Now, the basic formula of domestic cement slurry is: cement: water = 1:1 ~ 0.8. Sometimes, in order to increase the setting speed of the cement slurry, a small amount of water glass is added. The strength of cement slurry after solidification is generally 10MPa, and the stone formation rate is about 70%. [0004] At present, there are two main formulations of domestic cement slurry: [0005] The formula of the first common cement slurry is: cement: water = 1:1 ~ 0.8. The strength of cement slurry after solidification is generally 10MPa, and the stone formation rate is about 70%. The shortc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/38C04B22/08
Inventor 张景张文平白云峰李凯琦
Owner SHANXI LUAN ENVIRONMENTAL ENERGY DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com