Method for producing low-temperature cement clinker from straw ash
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of cement clinker and straw ash, which is applied in cement production and other directions to achieve the effect of reducing CO2 emissions, reducing pollution and good wear resistance.
Inactive Publication Date: 2013-04-17
淮安市水泥厂有限公司 +1
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The purpose of the present invention is to solve the problem that the above-mentioned straw ash will cause serious pollution to air and water sources, and to provide a kind of advanced and reasonable technology, low energy consumption, high benefit, low investment, no secondary pollution, and beneficial to the large-scale use of straw ash. Method for producing low-temperature cement clinker from environmentally friendly straw ash
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] The straw ash of the present invention produces low-temperature cement clinker, which is prepared by using dry and wet straw ash as the main raw material and steel slag and aluminum slag as auxiliary materials through a special process. The production method includes the following steps:
[0016] 1) Material preparation: The raw materials are straw ash, steel slag and aluminum slag; the straw ash is the fuel of various plant stalks such as rice stalk, wheat stalk, rice husk, corn stalk, soybean stalk, wood top branches and bark used in power plants The dry and wet waste slag discharged after combustion and power generation is called straw ash, and the steel slag used is the waste slag discharged from the iron and steel plant. Aluminum slag is the waste slag discharged from the production of aluminum sulfate in chemical plants, containing A 2 O 3 At about 15%, the water content is about 40%, and the PH value is less than 6.
[0017] 2) Ingredients and balls;
[0018] ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
A method for producing low-temperature cement clinker by using straw ash according to the present invention mainly comprises such steps as material preparation, batching and balling, steam curing and low-temperature calcining, and grinding. Cement having low-temperature cement clinker that rivals cement having silicate cement clinker can be produced by using the dry and wet straw ash as the main raw material and using steel slag and aluminum slag as the auxiliary material. This cement has multiple features such as high cement strength, desirable concrete compatibility, good abrasion resistance, low heat of hydration, micro expansion, good frost resistance, and good corrosion resistance, and can be directly used in building construction such as dams, underwater projects, roads, bridges, and civil projects. The production method of the cement has the advantages such as a simple and proper process, low energy consumption, high benefit, low investment, and no secondary pollution, and further facilitates the environment protection. In comparison with the existing production method of common cement, the production method of the present invention saves the investment by 80%, reduces the cost of the cement by 60%, reduces the energy consumption by 80%, decreases the CO2 emission by 80%, and can greatly consume the straw ash and other industrial waste slag, thereby reducing environmental pollution. The production method of the present invention is a good method capable of turning waste into treasure and facilitating the environment protection.
Description
technical field [0001] The invention is a method for producing a new type of low-temperature cement clinker by using straw ash, steel slag and aluminum slag, especially for the current power plants using various plant stalks, such as rice straw, wheat straw, rice husk, corn stalk, soybean stalk, The dry and wet waste residues discharged from burning wood top bark and other power generation are called straw ash. Using advanced technology to produce a new type of low-temperature cement clinker, the straw ash is a kind of harmless treatment method, which belongs to green environmental protection or cement field. Background technique [0002] From the domestic and international situation, the United States began to develop and utilize straw ash in the 1970s, followed by Japan, Australia, New Zealand, India, Thailand and other countries that studied straw ash and used it to mix cement and concrete admixtures. Studies have reported that the utilization is about 60%. At present, ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more