Preparation method for dental coloring zirconia blank
A technology of zirconium oxide and zirconium oxychloride, used in dental preparations, dental prostheses, dentistry, etc., can solve the problems of difficult uniform distribution of colorants, and achieve the effects of low cost, industrialization, and simple preparation process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] First take 136.8g zirconium oxychloride as raw material, 17.1g yttrium nitrate as stabilizer, 0.08g praseodymium nitrate, 0.1g gadolinium nitrate, and 0.2g erbium nitrate as colorants to prepare colored nano-zirconia powder by co-precipitation method, and then The prepared zirconia powder is directly isostatically pressed under a pressure of 100 MPa. Finally, the formed body is pre-sintered in a sintering furnace at 1050°C.
Embodiment 2
[0024] First, 136.8g of zirconium oxychloride was used as raw material, 12.6g of yttrium acetate as stabilizer, 1.6g of dysprosium acetate, 0.2g of neodymium acetate, and 0.2g of europium acetate were used as colorants to prepare colored zirconia powder by hydrothermal method, and then the prepared The zirconia powder is directly isostatically pressed under a pressure of 1000MPa. Finally, the formed body is pre-sintered in a sintering furnace at 800°C.
Embodiment 3
[0026] First, 136.8g of zirconium oxychloride was used as raw material, 9.3g of yttrium chloride as stabilizer, 1.0g of cerium chloride, 0.3g of neodymium chloride, and 0.6g of erbium chloride as colorants to prepare colored nano-zirconia powder by sol-gel method body, and then the prepared zirconia powder is formed by dry pressing at 40MPa and directly isostatically pressing at 500MPa. Finally, the shaped body is pre-sintered in a sintering furnace at 1200°C.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap