Method for internalization of storage batteries of electric bicycle

A technology for electric bicycles and batteries, which is applied in the production process of batteries and the internal formation of electric bicycle batteries. It can solve the problems of inconsistent battery response, difficulty in achieving absolute consistency in the weight of lead paste, and long charging time.

Active Publication Date: 2015-04-01
FENGFAN
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the grid is cast, it needs to be hardened. The hardening time is generally 72-168 hours. During this time, a dense oxide film will be formed on the surface of the grid. The thickness of the oxide film dissolves, and the thickness of the oxide film will cause the battery to respond inconsistently during charging; it is also difficult to achieve an absolute consistency in the weight of the paste when coating the board. The reaction with a small amount of paste is fast, and the response with a large amount of paste is slow. This is also the factor that causes the inconsistency of the battery formation reaction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for internalization of storage batteries of electric bicycle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1: The main process parameters of 16 stages of electric bicycle storage battery internalization are as follows:

[0034] Phase Charging Method Current Time

[0035] 1 reverse charge 0.9A 20 minutes,

[0036]2 Charge 1.3A for 1 hour,

[0037] 3 Charge 3.5A for 5 hours,

[0038] 4 Charging 2.6A 8 hours,

[0039] 5 Charging 1.1A for 3 hours,

[0040] 6 discharge -2.4A 2.5 hours,

[0041] 7 Charging 3.5 A 3.5 hours,

[0042] 8 Charge 2.4 A for 4 hours,

[0043] 9 Discharge -3.6 A for 1 hour,

[0044] 10 charging 3.4 A 4 hours,

[0045] 11 Charge 2.4 A for 4 hours,

[0046] 12 Charge 1.0 A for 1 hour,

[0047] 13 discharge -4A for 2 hours,

[0048] 14 Charge 2.6 A for 4 hours,

[0049] 15 Charge 1.3 A for 4 hours,

[0050] 16 Charging 4 A 0.5 hours.

[0051] In the above-mentioned 16th stage, the four accumulators forming the battery pack of the electric bicycle are connected in parallel as a group, and are charged with a constant voltage of 14.8V. ...

Embodiment 2

[0052] Embodiment 2: The main process parameters of 16 stages of electric bicycle storage battery internalization are as follows:

[0053] Phase Charging Method Current Time

[0054] 1 Reverse charging 1.1A for 10 minutes,

[0055] 2 charging 1.2A 1.3 hours,

[0056] 3 charging 3.6A 4.5 hours,

[0057] 4 Charging 2.6A 7 hours,

[0058] 5 Charging 1.0A 3.5 hours,

[0059] 6 discharge -2.5A 2.3 hours,

[0060] 7 Charging 3.4 A 4 hours,

[0061] 8 Charging 2.5 A 3.5 hours,

[0062] 9 Discharge -3.2 A for 2 hours,

[0063] 10 charging 3.5 A 3.5 hours,

[0064] 11 Charging 2.5 A 3.5 hours,

[0065] 12 Charge 1.1 A for 1 hour,

[0066] 13 discharge -6A for 1 hour,

[0067] 14 Charge 2.4 A for 5 hours,

[0068] 15 Charging 1.2 A 4.5 hours,

[0069] 16 Charge 3 A 0.8 hours.

[0070] In the above-mentioned 16th stage, the four accumulators forming the battery pack of the electric bicycle are connected in parallel as a group, and are charged with a constant voltage of 14.8...

Embodiment 3

[0071] Embodiment 3: The main process parameters of 16 stages of electric bicycle storage battery internalization are as follows:

[0072] Phase Charging Method Current Time

[0073] 1 Reverse charging 1.0A for 15 minutes,

[0074] 2 Charging 1.1A 1.5 hours,

[0075] 3 charging 3.7A for 4 hours,

[0076] 4 Charging 2.4A 9 hours,

[0077] 5 charging 0.9A for 4 hours,

[0078] 6 discharge -2.6A for 2 hours,

[0079] 7 Charging 3.6 A for 3 hours,

[0080] 8 Charge 2.6 A for 3 hours,

[0081] 9 Discharge -3.5 A for 1.5 hours,

[0082] 10 Charge 3.6 A for 3 hours,

[0083] 11 Charge 2.6 A for 3 hours,

[0084] 12 charging 0.9 A 1.5 hours,

[0085] 13 Discharge -5A for 1.5 hours,

[0086] 14 Charging 2.5 A 4.5 hours,

[0087] 15 Charge 1.1 A for 5 hours,

[0088] 16 Charge 2 A for 1 hour.

[0089] In the above-mentioned 16th stage, the three batteries that make up the electric bicycle battery pack are connected in parallel as a group, and charged with a constant voltag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for the internalization of storage batteries of an electric bicycle, which is used for solving the problem of cycle life loss caused by inconsistent voltage of all storage batteries. The method comprises a plurality of charging and discharging stages and is characterized in that: in the last stage for charging and discharging, several storage batteries constituting a storage battery pack of the electric bicycle are connected in parallel to form a group and are changed for 0.5-1 hour by adopting the constant voltage of 14.8V and the limited current of 2-4A. According to the invention, reverse charging is performed in the first stage of the internalization to solve the problems of larger initial electric internal resistance and heat generation; and in the last stage, several storage batteries of the storage battery pack of the electric bicycle are connected in parallel to form a group and are charged by adopting the constant voltage of 14.8V and the limited current of 2-4A, so that the problem of life loss of the storage batteries due to inconsistency is solved completely. By means of the method disclosed by the invention, the consistency of the internalization of the storage batteries of the electric bicycle can be increased, so that the service life of the storage batteries can be prolonged.

Description

technical field [0001] The invention relates to a storage battery production process, in particular to a storage battery internalization method for an electric bicycle, and belongs to the technical field of storage batteries. Background technique [0002] As a means of transportation, electric bicycles have the characteristics of lightness, environmental protection, convenience, and economy. In recent years, the sales of electric bicycles have been increasing year by year, and they are more and more popular among people. At the same time, consumers have higher and higher quality requirements for electric bicycles. The battery is one of the key components of the electric bicycle. The power of the electric bicycle comes from the battery, and the cycle life of the battery becomes the key performance of the battery. There are many reasons for the termination of battery cycle life, the main reason being that the voltage of each battery in the whole battery pack is inconsistent. A...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/12H01M10/44
CPCY02T10/7016Y02E60/126Y02E60/10Y02P70/50
Inventor 任建华张文龙李亚辉陈志雪刘燕朝
Owner FENGFAN