High-performance ceramic friction sheet and production process thereof

A production process and friction plate technology, applied in the field of high-performance ceramic friction plates and their production processes, can solve the problems of easy scratching of friction pairs, unstable friction performance, short service life, etc., and achieve good compressive strength and friction coefficient. Moderate, low wear rate effect

Active Publication Date: 2014-06-25
浙江台基摩擦材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing non-ceramic friction materials have the following disadvantages: first, the friction performance is unstable; second, the service life is short; third, the noise is relatively large;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041] Below in conjunction with specific embodiment the present invention will be further described:

[0042] A high-performance ceramic friction plate is composed of the following parts by weight: copper: 60-68 parts; iron: 10-15 parts; tin: 2-5 parts; silicon dioxide: 5-10 parts; molybdenum disulfide: 3-8 parts; calcium aluminate: 5-10 parts; graphite: 5-13 parts; kerosene: 0.5-1.5 parts.

[0043] The particle size or form of the above substances are: copper: ≤200 mesh; iron: 150 mesh to 200 mesh; tin: ≤200 mesh; silicon dioxide: ≤100 mesh; molybdenum disulfide: colloidal powder; calcium aluminate: ≤100 mesh ; Graphite: ≤ 100 mesh; Kerosene: liquid.

[0044] A production process of a high-performance ceramic friction plate is prepared according to the following steps:

[0045] (1) Mixture:

[0046] 1) Weigh graphite and molybdenum disulfide in specified parts by weight and load them into trays respectively, and put them into a drying box for drying. Hours, then cool to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
dispersion coefficientaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of friction sheets, and relates to a high-performance ceramic friction sheet and a production process thereof. The high-performance ceramic friction sheet consists of the following substances in parts by weight of: 60 to 68 parts of copper, 10 to 15 parts of ferrum, 2 to 5 parts of tin, 5 to 10 parts of silica, 3 to 8 parts of molybdenum disulfide, 5 to 10 parts of calcium aluminate, 5 to 13 parts of graphite and 0.5 to 1.5 parts of kerosene. The production process of the friction sheet comprises the following steps of: mixing materials; pressing and forming; and sintering and detecting under a dry working environment. The high-performance ceramic friction sheet has the beneficial effects of high friction performance, high compression strength and low abrasion rate; and when the high-performance ceramic friction sheet is used, the number of produced gas and the number of produced powder are small, the environment pollution is low, and the high-performance ceramic friction sheet brakes steadily, softly, safely and reliably.

Description

technical field [0001] The invention belongs to the technical field of friction plates, in particular to a high-performance ceramic friction plate and its production process. Background technique [0002] Friction material is a component material used in power machinery that relies on friction to perform braking and transmit kinetic energy. Any mechanical equipment and various moving vehicles must have braking or transmission devices. Friction material is a critical component on this braking or transmission. Its main function is to absorb or transmit power through friction. For example, the clutch plate transmits power, and the brake plate absorbs kinetic energy. They enable mechanical equipment and various motor vehicles to work safely and reliably. So the friction material is a widely used and crucial material. [0003] Especially in recent years, with the rapid development of the automobile industry, people have higher and higher requirements for braking performance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00C22C32/00C22C9/00B22F3/16F16D69/02
Inventor 郑士洋
Owner 浙江台基摩擦材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap