Modified rubber and preparation method thereof

A modified rubber and modification technology, which is applied in the field of preparation of nano-silica/polyconjugated diene composite emulsion and its modified rubber, can solve the problems of difficult dispersion, easy sedimentation loss, quality loss, etc., and achieve anti- Excellent wet skid performance and shock absorption performance, easy handling, and improved tensile strength

Active Publication Date: 2014-04-02
PETROCHINA CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The physical and mechanical properties and dynamic mechanical properties of the rubber compound prepared by this method are better, but a large amount of organic alcohol, cyclohexane, etc. Solvent, during the solvent removal process, it is difficult for the macromolecular chain to cover all the silica particles-agglomeration, there will be mass loss, and it may also aggregate in the co-coagulation gel matrix, making it difficult to achieve good dispersion
[0005] Ye Xin et al disclosed a preparation method of silica / styrene-butadiene rubber composite material by wet compounding technology in "Rubber Science and Technology Market" 2009 No. 10. In this method, the white carbon black in the water phase The surface of carbon black is organically modified, and then mixed with styrene-butadiene latex to coagulate to prepare the modified silica / styrene-butadiene rubber composite material. The biggest advantage of this method is that the filler has better dispersion and can effectively avoid the flying of the filler. Pollution, but silica is easy to settle and lose in the wet compounding process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Surface functional modification of nano-silica: Weigh 120g of nano-silica and dry it in an oven, then mix it with 1200g of toluene and then ultrasonically disperse it fully, add 240g of hydrolyzed VTES, stir and heat to 82°C for 2.3 hours, then filter, Wash, vacuum dry.

[0050] Functional emulsion preparation:

[0051] The first step is the preparation of monomer pre-emulsion. 1,200 g of 1,3-butadiene, 120 g of sodium dodecylbenzenesulfonate, 1,800 g of deionized water, 12 g of sodium hydroxide, and 2.4 g of potassium persulfate were mixed and pre-emulsified for 20 minutes to prepare a pre-emulsion.

[0052] In the second step, the functional emulsion is prepared with the modified nano-silica as the core. Take 3.6g of nano-silica modified by surface functionalization and add it to a reactor containing 60g sodium dodecylbenzenesulfonate and 480g deionized water, stir and heat up to 60°C, and then take 313g monomer pre-emulsion Add it into the reactor, control the tem...

Embodiment 2

[0055] According to the method disclosed in "Journal of Radiation Research and Radiation Technology", Volume 25, No. 5, "Study on Surface Modification of Nano-Silicon Dioxide and Radiation-Initiated Grafting GMA" in 2007, the nano-silicon dioxide method for surface functional modification: Weigh 6g of nano-silicon dioxide and dry it in an oven at 50°C for 5h, add the dried nano-silicon dioxide into an aqueous solution in which 96g of coupling agent MPS is dissolved, and ultrasonically disperse for 1h. After dispersion, the mixture was stirred at 110°C for 8h. After filtration, the modified silicon dioxide is washed with toluene, and the obtained product is vacuum filtered, then extracted by Soxhlet, and finally placed in an oven for drying.

[0056] Functional emulsion preparation:

[0057] The first step is the preparation of monomer pre-emulsion. 1200 g of isoprene, 72 g of sodium lauryl sulfate, 1200 g of deionized water, 6 g of ammonia water, and 9.6 g of ammonium persul...

Embodiment 3

[0061] Surface functional modification of nano-silica: Weigh 240g of nano-silica and dry it in an oven for use, then mix it with 4800g of xylene and ultrasonically disperse fully, add 312g of hydrolyzed VTMS, stir and heat to 93°C for 4 hours to reflux , then filtered, washed, and dried in vacuum.

[0062] Functional emulsion preparation:

[0063] The first step is the preparation of monomer pre-emulsion. Prepare by mixing 1200g of 1,3-pentadiene, 40g of sodium dodecylbenzenesulfonate, 200g of alkylphenol polyoxyethylene ether, 1920g of deionized water, 9.6g of sodium carbonate and 9.8g of sodium persulfate for 30 minutes into a pre-emulsion.

[0064] In the second step, the functional emulsion is prepared with the modified nano-silica as the core. Get 54g of surface-functionalized modified nano-silica and add it to a reactor equipped with 54g fatty acid soap and 456g deionized water, stir and heat up to 68°C, then get 676g monomer pre-emulsion and add it to the reactor, co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified rubber and a preparation method thereof. The modified rubber is prepared by mixing rubber latex (1) and a nano-silica / poly(conjugated diene) composite emulsion (2) and carrying out coagulation and demulsification coprecipitation, wherein a mass ratio of the dry basis of the rubber latex to the dry basis of the nano-silica / poly(conjugated diene) composite emulsion is 100: (0.1 to 100); based on the dry basis of the nano-silica / poly(conjugated diene) composite emulsion, the nano-silica / poly(conjugated diene) composite emulsion comprises 0.1 to 5 parts of surface functionalization-modified nano-silica; the nano-silica / poly(conjugated diene) composite emulsion has granularity of 50 to 80nm, number-average molecular weight of 100000 to 120000 and molecular weight distribution of 2 to 3; and the rubber latex is a homopolymer or a copolymer containing a poly(conjugated diene) compound and is prepared by emulsion polymerization.

Description

technical field [0001] The invention relates to a modified rubber and a preparation method thereof, in particular to a nano-silica / polyconjugated diene composite emulsion and a preparation method of the modified rubber. Background technique [0002] In recent years, the preparation of organic polymer / inorganic nanoparticle composites has become one of the hot research topics in various countries. With the development of automobiles in the direction of high speed, safety, energy saving and comfort, the requirements for high performance tires are also increasing year by year, which requires tire treads to have good wet skid resistance, excellent wear resistance and low rolling resistance. [0003] Nano-silica, commonly known as white carbon black, is the second largest reinforcing agent used in the rubber industry after carbon black. Since the 1990s, silica has been widely used as a reinforcing filler in tire tread formulations, so that the above-mentioned "devil triangle" p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/08C08L9/04C08L13/02C08L9/00C08L11/02C08K9/06C08K3/36C08F136/06C08F136/08C08F136/04C08F2/44C08F2/24C08C1/14
Inventor 赵志超马朋高李晓艳胡育林李波龚光碧郑聚成贾慧青王永峰梁滔秦传高翟云芳邵卫陈建刚肖晔
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com