Cobalt salt bonding agent for bonding natural rubber and naked steel framework and preparation method thereof

A natural rubber and adhesive technology, applied in the directions of adhesive additives, aldehyde/ketone condensation polymer adhesives, adhesives, etc., can solve the problems of inability to adapt, the adhesive ability of modified cobalt salt adhesives is reduced, etc., and achieves convenient operation. , the use effect is obvious, the effect of low price

Inactive Publication Date: 2012-04-18
镇江泛华新材料科技发展有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to reduce the cost of rubber products, many rubber product manufacturers use a large amount of reclaimed rubber and reclaimed rubber powder in the formula of rubber products. Although the reclaimed rubber has been desulfurized, the rubber molecular chain is not completely linear. The powder is vulcanized mature rubber, which is almost completely reticulated, which makes the adhesive ability of the coated modified cobalt salt adhesive mainly chemically bonded and rubber as the carrier drop sharply, and cannot adapt to this type of rubber. The needs of product manufacturers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cobalt salt bonding agent for bonding natural rubber and naked steel framework and preparation method thereof
  • Cobalt salt bonding agent for bonding natural rubber and naked steel framework and preparation method thereof
  • Cobalt salt bonding agent for bonding natural rubber and naked steel framework and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] Below in conjunction with specific embodiment, further illustrate the present invention, should be understood that these embodiments are only used to illustrate the present invention and are not intended to limit the scope of the present invention, after having read the present invention, those skilled in the art will understand various equivalent forms of the present invention All modifications fall within the scope defined by the appended claims of the present application.

[0020] A cobalt salt adhesive for bonding natural rubber and bare steel framework, including a composite adhesive, phenolic resin and auxiliary agents, the composite adhesive is composed of a main adhesive and a co-adhesive, wherein the main adhesive includes boroacylated cobalt and new Cobalt decanoate, vanadium 2-ethylhexanoate as an adhesive promoter, methyl donor and methyl acceptor in phenolic resin, toughening agent, activator, vulcanization activator, silane coupling agent, vulcanization age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cobalt salt bonding agent for bonding natural rubber and a naked steel framework and a preparation method thereof. The bonding agent comprises a compound bonding agent, a phenolic resin and an aid, wherein the compound bonding agent consists of a main bonding agent and an auxiliary bonding agent; the main bonding agent comprises cobalt boroacylate and cobalt neodecanoate; the auxiliary bonding is 2- ethyl vanadium caproate; the phenolic resin comprises a methyl donor and a methyl acceptor; and the aid comprises a toughening agent, an activating agent, a vulcanizing activator, a silane coupling agent and a vulcanizing agent. The cobalt salt bonding agent for bonding natural rubber and the naked steel framework is obtained by dispersing the compound bonding agent into a phenolic resin carrier, adding the aid, and dissolving into adhesive cement by using a mixed solvent. The cobalt salt bonding agent has the advantages of high thermal stability, high dynamic property, direct coating and low cost, an is suitable for high-strength bonding of natural rubber containing reclaimed rubber or reclaimed rubber powder such as natural rubber and mixed rubber consisting of the natural rubber and general synthetic rubber with a naked steel framework material.

Description

technical field [0001] The present invention relates to an adhesive and a preparation method thereof, especially for bonding natural rubber containing reclaimed rubber or reclaimed rubber powder, including natural rubber and its mixed rubber with general-purpose synthetic rubber, to bare steel framework, for bonding natural rubber to bare steel framework Cobalt salt binder and its preparation method. Background technique [0002] In the continuous production of large-scale rubber products such as steel radial tires, steel wire reinforced conveyor belts, and steel wire braided rubber hoses, the high-strength bonding of elastomers such as rubber and galvanized or brass-plated steel wire cord braided skeleton materials is usually bonded directly. Addition-type cobalt salt binders, direct-addition cobalt salt binders include cobalt stearate, solid cobalt naphthenate, cobalt neodecanoate, cobalt boroacylate, etc. These cobalt salt binders, especially cobalt boroacylate, have In ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/32C09J11/06
Inventor 严忠庆陈秀娟
Owner 镇江泛华新材料科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products