A kind of composite polyolefin material and its preparation method and application

A composite polyolefin and polyolefin technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problems of fire prevention and fire, and achieve the effect of light weight and multiple times of reuse

Active Publication Date: 2016-02-03
HEFEI GENIUS NEW MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, bamboo fences, wooden templates, or temporarily unused square logs on the construction site can be used as platforms for workers to stand and store tools; among them, bamboo fences are used the most, and their main disadvantage is that they cannot be fireproof, so when building a building frame, if The high-temperature welding slag dripping from electric welding often causes fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite polyolefin material and its preparation method and application
  • A kind of composite polyolefin material and its preparation method and application
  • A kind of composite polyolefin material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] (1) The proportion of each component of the outer layer material is as follows:

[0055] Polypropylene: 64.8 parts,

[0056] Nitrogen-phosphorus halogen-free flame retardant: 35 parts,

[0057] Antioxidant 1010: 0.1 parts,

[0058] Lubricant EBS: 0.1 parts,

[0059] Among them, the nitrogen-phosphorus halogen-free flame retardant is a compound of ammonium polyphosphate and melamine urate, and the compounding ratio is 2:1;

[0060] The above-mentioned mixture is fed into the twin-screw extruder by a feeder with precise metering, and is sheared at high speed by the twin-screw, kneaded, extruded from the machine head, drawn, air-cooled, pelletized and dried; the twin-screw The technological parameters of the screw extruder are as follows: the temperature of each section of the screw should be controlled between 170 and 190 °C.

[0061] (2) The proportion of each component of the inner layer material is as follows:

[0062] Polypropylene: 50 parts,

[0063] Glass fibe...

Embodiment 2

[0071] (1) The proportion of each component of the outer layer material is as follows:

[0072] Polypropylene: 56.2 parts,

[0073] Talcum powder: 20 parts,

[0074] Decabromodiphenylethane: 18 parts,

[0075] Antimony trioxide: 5 parts,

[0076] Antioxidant 1010: 0.2 parts,

[0077] Antioxidant 168: 0.2 parts,

[0078] Lubricant EBS: 0.4 parts;

[0079] The above-mentioned mixture is fed into the twin-screw extruder by a feeder with precise metering, and is sheared at high speed by the twin-screw, kneaded, extruded from the machine head, drawn, air-cooled, pelletized and dried; the twin-screw The technological parameters of the screw extruder are as follows: the temperature of each section of the screw should be controlled between 170 and 190 °C.

[0080] (2) The proportion of each component of the inner layer material is as follows:

[0081] Polypropylene: 69.5 parts,

[0082] Mica: 30 parts,

[0083] Antioxidant 1010: 0.1 parts,

[0084] Antioxidant 168: 0.1 parts...

Embodiment 3

[0090] (1) The proportion of each component of the outer layer material is as follows:

[0091] Polypropylene: 79.4 parts,

[0092] Octabromoether: 16 parts,

[0093] Antimony trioxide: 4 parts,

[0094] Antioxidant 1010: 0.1 parts,

[0095] Antioxidant 168: 0.1 parts,

[0096] Lubricant EBS: 0.4 parts;

[0097] The above-mentioned mixture is fed into the twin-screw extruder by a feeder with precise metering, and is sheared at high speed by the twin-screw, kneaded, extruded from the machine head, drawn, air-cooled, pelletized and dried; the twin-screw The technological parameters of the screw extruder are as follows: the temperature of each section of the screw should be controlled between 170 and 190 °C.

[0098] (2) The proportion of each component of the inner layer material is as follows:

[0099] Polypropylene: 77.7 parts,

[0100] Talc powder: 10 parts,

[0101] E-glass fiber: 10 parts,

[0102] Bismaleimide: 2 parts,

[0103] Antioxidant 1010: 0.1 parts,

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of high molecular materials, and relates to a composite polyolefin material, a preparation method and a use of the composite polyolefin material. The material comprises 9 parts of an outer layer flame-retardant polyolefin material and 1-4 parts of an inner layer reinforced polyolefin layer, wherein the outer layer flame-retardant polyolefin material is prepared from the following components in parts by weight: 50-80 parts of polyolefin 1, 0-30 parts of a filler 1, 16-35 parts of a fire retardant, 0-9 parts of a flame retardant synergist, 0.1-0.4 part of an antioxidant 1 and 0.1-0.4 part of a lubricating agent 1; and the inner layer reinforced polyolefin layer is prepared from the following components in parts by weight: 50-80 parts of polyolefin 2, 0-45 parts of a glass fiber, 0-30 parts of the filler 2, 0-5 parts of a graft, 0.1-0.4 part of an antioxidant 2 and 0.1-0.4 part of a lubricating agent 2. The material has the advantages of being low in cost, light in weight, good in toughness balance, changeable in size and fireproofing, and being capable of being used for a plurality of times.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a composite polyolefin material and its preparation method and application. Background technique [0002] With the development of the construction industry, construction formwork plays an increasingly important role in it. At present, steel formwork, wood formwork and plastic formwork are widely used. Although the steel formwork has a solid structure and can be used repeatedly, it has the disadvantages of heavy weight, poor corrosion resistance, and difficult demoulding; the wooden formwork can be cut arbitrarily in structure, but it is easy to deform after being exposed to moisture, and the number of repeated uses is small and easy. Burning disadvantages. The plastic formwork is favored by the construction industry due to its light weight, corrosion resistance, and water resistance, but it has not been widely used at present. The reason is that in addition to the insuf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/32B32B27/18C08L23/12C08L23/06C08K13/02C08K13/04C08K7/14B29C47/38B29C70/60E04G9/05B29C48/395
CPCB29C48/0022B29C48/04B29C48/40
Inventor 石允慧孙利明
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com