A kind of interior wall insulation coating

A technology for thermal insulation coatings and interior walls, applied in the direction of reflection/signal coatings, coatings, etc., can solve problems such as high building energy consumption, heat loss, unfairness, etc.

Active Publication Date: 2016-03-16
HAINAN SEQUOIA CREATION
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current building energy-saving and thermal insulation measures are only aimed at the outer envelope of the building. Generally, no thermal insulation measures are used between the partition walls of the buildings in the building. In this way, different buildings may have different temperatures, resulting in thermal pressure. A room experiences heat loss, the flow of heat from a warmer room to a cooler room
This unfair phenomenon of heat use is likely to cause various problems and contradictions. For example, the heat loss in the household is serious, which makes the heat use uneven among neighbors, resulting in unfair phenomena, and has high building energy consumption, thus Influenced the promotion of my country's building energy conservation policy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of interior wall insulation coating
  • A kind of interior wall insulation coating
  • A kind of interior wall insulation coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0079] The present invention has no special limitation on the preparation method of the interior wall thermal insulation coating, and the preparation method of the interior wall coating well-known to those skilled in the art can be adopted. In the present invention, the interior wall thermal insulation coating is preferably prepared according to the following method:

[0080] Mixing water, additives and inorganic fillers to obtain a mixture;

[0081] ultrafine the mixture to obtain ultrafine particles;

[0082] mixing the ultra-fine particles with infrared reflective pigments with a refractive index of 2.0 or more and a particle size of not less than 1 μm, doped semiconductors and metal powders to obtain a slurry;

[0083] The slurry is mixed with a coating resin to obtain an interior wall thermal insulation coating.

[0084] In the invention, water, additives and inorganic fillers are firstly mixed to obtain a mixture. In the present invention, there is no special limitati...

Embodiment 1

[0109] 5 g of TiO with a particle size of 5 μm 2 Add 200mL distilled water to form a slurry, add 0.1g sodium hexametaphosphate and stir to make TiO 2 fully dispersed; then 1gNa 2 CO 3 Dissolve 2.5g of direct light-fast turquoise blue GL in hot water at 85°C to 90°C, add the obtained color pigment solution into the above slurry after proper stirring, adjust the pH of the reaction solution and keep it constant, and carry out constant temperature coloring for 2.5 hours ; the BaCl 2 Dissolve in hot water at 80°C, add to the above-mentioned colored solution in 5 times, and then add OP emulsifier and color-fixing agent Y diluted with water in turn; after stirring and mixing for 3 hours, wash, filter and After drying, a colored infrared reflective pigment is obtained.

Embodiment 2

[0111] In parts by weight, add 22 parts of water into the batching tank, add 1 part of sodium polyphosphate, 2 parts of alcohol ester twelve, 1 part of silicone defoamer, 1 part of propylene glycol and 1 part of cellulose ether to thicken After stirring evenly, add 22 parts of ordinary titanium dioxide with a particle size of 1 μm, and disperse the obtained mixture at a speed of 100 rpm; then superfine the dispersed mixture under the strong shear of a high-speed disperser ; Add 20 parts of rutile titanium dioxide with a particle size of 6 μm to the ultra-fine mixture, and disperse evenly; then add 30 parts of acrylate emulsion to it, and disperse to obtain the base paint;

[0112] Adding defoamer, leveling agent and thickener to the obtained base paint to adjust the required viscosity to obtain the interior wall thermal insulation paint.

[0113] The performance of the coating that the present invention detects obtains, concrete process is as follows:

[0114] "GB / T9756-2009 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
refractive indexaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an interior wall heat insulation coating. The coating comprises the following components in parts by weight: 5-45 parts of water, 3-25 parts of auxiliaries, 3-55 parts of inorganic fillers, 5-55 parts of coating resins and 1-30 parts of infrared reflection pigments with refractive indexes being over 2.0 and grain sizes being not less than 1mu m, doped semiconductors and metal powder. In the invention, the infrared reflection pigments with refractive indexes being over 2.0 and grain sizes being not less than 1mu m and the metal powder can reflect most mid-far infrared heat radiation to the interior instantaneously; and the doped semiconductors enable the wall surface to have lower heat radiation absorption and high heat storage coefficient and further enable the temperature of the wall surface to rise, thus increasing the indoor temperature, greatly improving the thermal comfort degree of a room and further improving the indoor heat insulation effect. Therefore, the interior wall heat insulation coating provided by the invention has a better heat insulation effect.

Description

technical field [0001] The invention relates to the technical field of thermal insulation materials, in particular to a thermal insulation coating for interior walls. Background technique [0002] At present, the heating method commonly used in my country is mainly radiator convection heating mode, such as floor heating, radiators, etc. Radiation heating systems such as infrared electrothermal film are gradually popularized because of more uniform heat distribution and higher thermal efficiency on the human body and other objects. Indoor heat conduction is mainly radiation and convection. Regardless of whether convection heating or radiation heating is used, heat radiation plays an important role in the indoor heat effect. When heat radiation reaches the surface of the wall, it will be absorbed by the wall and be lost to the outside. [0003] Heating energy consumption in winter is the main energy consumption of Chinese buildings, and the Chinese government has continuously ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D125/14C09D133/04C09D7/12C09D5/33
Inventor 王忠
Owner HAINAN SEQUOIA CREATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com