Cast-rolling method of double-zero aluminum foil
A double-zero aluminum foil, casting and rolling technology, applied in the field of alloys, can solve the problems of small elongation, rough surface of double-zero foil, many pinholes, etc., and achieve the effect of less pores, uniform structure, high strength and elongation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] A method of preparing double zero aluminum foil is:
[0022] S 1 Degassing and deslagging: use a refining agent to degas and deslag the aluminum alloy melt. After the treatment, the hydrogen content of the melt is 0.15ml / 100g;
[0023] S 2 Casting and rolling: casting and rolling the melt obtained in S1, the thickness of the cast and rolling finished product is 6.5mm;
[0024] S 3 Cold rolling: cold rolling the cast and rolled finished product obtained in S2 to a thickness of 2.5 mm;
[0025] S 4 Uniform annealing: the cold-rolled finished product obtained in S3 is subjected to homogenization annealing at 450°C for 20 hours and then air-cooled; to eliminate segregation in grain boundaries and refine grains;
[0026] S 5 Cold rolling: secondary cold rolling of the annealed product obtained in S4 to a thickness of 0.6 mm;
[0027] S 6 Annealing: Perform intermediate annealing on the cold-rolled product obtained in S5 at 340°C; eliminate internal stress to continue...
Embodiment 2
[0033] A method of preparing double zero aluminum foil is:
[0034] S 1 Degassing and deslagging: use a refining agent to degas and deslag the aluminum alloy melt, and the hydrogen content of the melt after treatment is 0.13ml / 100g;
[0035] S 2 Casting and rolling: casting and rolling the melt obtained in S1, the thickness of the cast and rolling finished product is 6.6mm;
[0036] S 3 Cold rolling: cold rolling the cast and rolled finished product obtained in S2 to a thickness of 2.7 mm;
[0037] S 4 Uniform annealing: the cold-rolled finished product obtained in S3 is subjected to homogenization annealing at 460°C for 18 hours and then air-cooled; to eliminate segregation in grain boundaries and refine grains;
[0038] S 5 Cold rolling: secondary cold rolling of the annealed product obtained in S4 to a thickness of 0.58 mm;
[0039] S 6 Annealing: The cold-rolled product obtained in S5 is subjected to intermediate annealing at 350°C; internal stress is eliminated to...
Embodiment 3
[0045] A method of preparing double zero aluminum foil is:
[0046] S 1 Degassing and deslagging: use a refining agent to degas and deslag the aluminum alloy melt. After the treatment, the hydrogen content of the melt is 0.1ml / 100g;
[0047] S 2 Casting and rolling: casting and rolling the melt obtained in S1, the thickness of the cast and rolling finished product is 6.7mm;
[0048] S 3 Cold rolling: cold rolling the cast and rolled finished product obtained in S2 to a thickness of 2.9 mm;
[0049] S 4 Uniform annealing: the cold-rolled finished product obtained in S3 is subjected to homogenization annealing at 470°C for 16 hours and then air-cooled; to eliminate segregation in grain boundaries and refine grains;
[0050] S 5 Cold rolling: secondary cold rolling of the annealed product obtained in S4 to a thickness of 0.55 mm;
[0051] S 6 Annealing: The cold-rolled product obtained in S5 is subjected to intermediate annealing at 360°C; internal stress is eliminated to...
PUM
Property | Measurement | Unit |
---|---|---|
Elongation | aaaaa | aaaaa |
Elongation | aaaaa | aaaaa |
Elongation | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap