Method for preparing magnetism papermaking sizing agent stabilized by magnetism solid particle emulsification

A solid particle, emulsification stable technology, applied in papermaking, textiles, papermaking, paper, etc., can solve the problems of ASA emulsification process complexity, environmental pollution, clogged blankets, etc., to avoid adverse effects, reduce costs, and improve pollution effects

Inactive Publication Date: 2013-07-31
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, starch needs to be gelatinized and cooled before use, which makes the ASA emulsification process quite complicated, difficult to control, and often causes problems such as deposition and clogging of felts
The surfactant also brings certain adverse effects to sizing, and also brings certain pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The magnetic nano-Fe with a particle size of 20nm 3 o 4 Disperse in deionized water and ultrasonically disperse for 0.5h to obtain nano-Fe 3 o 4 The solid suspension with a mass fraction of 1.5%, adjusted the pH value to 3.5-4 with 0.1mol / L glacial acetic acid, added absolute ethanol, and added γ-methacryloxypropyltrimethoxysilane (KH -570); the volume ratio of water, ethanol and γ-methacryloxypropyltrimethoxysilane is 1:1:2; stir in a constant temperature water bath at 65°C for 5 hours, and then wash with absolute ethanol repeatedly by centrifugation after cooling to room temperature , and the obtained solid was dried at 60° C. to obtain KH-570 modified magnetic nanoparticles.

[0022] The modified magnetic nanometer solid particles were dispersed in deionized water and ultrasonically dispersed to obtain a water suspension with a mass fraction of magnetic solid particles of 0.1%. Alkenyl succinic anhydride and water suspension are mixed according to the volume rati...

Embodiment 2

[0025] Magnetic nanometer γ-Fe with a particle size of 35nm 2 o 3 Disperse in deionized water, ultrasonically disperse for 0.5h to form a solid suspension with a mass fraction of 2.0%, add the same volume of absolute ethanol as deionized water, adjust the pH value to 4-5 with 0.1mol / L dilute hydrochloric acid, gradually Add γ-glycidyloxypropyltrimethoxysilane (KH560) dropwise, by volume, water: ethanol: γ-glycidyloxypropyltrimethoxysilane = 1:1:4, 70°C constant temperature water bath Stir for 4 hours, cool to room temperature, and repeatedly centrifuge and wash with absolute ethanol, and dry the obtained solid at 60° C. to obtain KH-560 modified magnetic nanoparticles.

[0026] The modified magnetic nanometer solid particles were dispersed in deionized water and ultrasonically dispersed to obtain a water suspension with a mass fraction of magnetic solid particles of 0.5%. Alkenyl succinic anhydride and water suspension are mixed according to the volume ratio of 3: 2, and the...

Embodiment 3

[0028] Magnetic nanometer MeFe with a particle size of 30nm 2 o 4 Disperse the particles in deionized water, ultrasonically disperse for 1 hour to form a solid suspension with a mass fraction of 3.0%, add the same volume of absolute ethanol, adjust the pH value to 5-6 with 0.2mol / L glacial acetic acid, add γ- Chloropropyltriethoxysilane (KH550), by volume ratio, deionized water: ethanol: γ-chloropropyltriethoxysilane = 1:1:8, stirred in a constant temperature water bath at 85°C for 6h, cooled to room temperature Afterwards, it was centrifuged and washed repeatedly with absolute ethanol, and the obtained solid was dried at 60° C. to obtain KH-550 modified magnetic nanoparticles.

[0029] The modified magnetic nanometer solid particles were dispersed in deionized water and ultrasonically dispersed to obtain an aqueous suspension with a mass percentage of magnetic solid particles of 1.0%. Alkenyl succinic anhydride and water suspension are mixed according to the volume ratio of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a magnetism papermaking sizing agent stabilized by magnetism solid particle emulsification. The method comprises the steps of adding magnetism nanometer solid particles in the particle diameter of 18nm to 50nm into deionized water, carrying out ultrasonic dispersion, adding absolute ethyl alcohol, then adding a silane coupling agent, stirring, standing the solution, cooling the solution to room temperature, obtaining magnetism nanometer solid particles modified by the silane coupling agent, then dispersing the magnetism nanometer solid particles into deionized water, mixing the solution with alkenyl succinic anhydride oil liquid, carrying out high-speed shearing emulsification, and obtaining the magnetism papermaking sizing agent stabilized by the magnetism solid particle emulsification. The magnetism papermaking sizing agent with the stable magnetism solid particle emulsification prepared by the method allows a paper sheet to have water resistance, meanwhile has magnetism, and is high in sizing efficiency, simple in preparation, capable of allowing alkenyl succinic anhydride to be emulsified into Pickering type emulsion with quite high stability without addition of any superficial active agent, little in emulsion emulsifier dosage, high in stability and low in foam, toxicity and cost.

Description

technical field [0001] The invention relates to a preparation method of a magnetic sizing agent, in particular to a preparation method of a magnetic paper-making sizing agent which is emulsified and stable by magnetic nanometer solid particles. Background technique [0002] In the 20th century, the papermaking industry shifted from the acidic papermaking system to the medium-alkaline papermaking system, which was an innovative change in the papermaking process. It greatly improved the quality of paper and expanded the range of fillers, reduced pulp consumption and energy consumption, reduced environmental pollution, and extended the service life of equipment. service life. According to statistics, in the early 1980s in Europe, the cultural paper produced by medium and alkaline sizing accounted for 60% to 65% of the total cultural paper, and it reached 95% in the 1990s. Alkaline sizing ratio jumped from 15% to over 90%. Since 1989, China has started to use medium and alkali...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/16D21H17/14D21H17/69
Inventor 林兆云于得海李友明
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com