Hot dip plated steel sheet having excellent plating adhesiveness and method of manufacturing the same

An adhesive, hot-dip plating technology, applied in hot-dip plating process, transportation and packaging, coating, etc. Plateability, the effect of speeding up development

Inactive Publication Date: 2013-09-04
POHANG IRON & STEEL CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0020] However, plating adhesion cannot be sufficiently ensured by the above-mentioned related techniques

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot dip plated steel sheet having excellent plating adhesiveness and method of manufacturing the same
  • Hot dip plated steel sheet having excellent plating adhesiveness and method of manufacturing the same
  • Hot dip plated steel sheet having excellent plating adhesiveness and method of manufacturing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0091] In the present invention, a 1.0 mm thick cold-rolled full-hard steel plate having the composition of the following Table 1 is used as a base steel plate, and the base steel plate is oxidized under the conditions described in Table 2 in a direct combustion furnace, and then heated under conventional operating conditions Under the reduction annealing and hot-dip plating process.

[0092] In this case, for samples 1 to 5 in Table 1 below, 10% H at a dew point of -45°C 2 -90%N 2 The reduction annealing treatment is carried out in a mixed atmosphere, specifically, the heat treatment condition of the infiltration section is to keep at 800° C. for 1 minute.

[0093] Meanwhile, for samples 6 to 8 in Table 1 below, 25% H at a dew point of -45°C 2 -75%N 2 The reduction annealing treatment is carried out in the mixed atmosphere of the same method, and the heat treatment condition of the wet section is also kept at 800°C for 1 minute.

[0094] Hot-dip plating was also performed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is a hot dip plated steel sheet used in automotive materials and a method of manufacturing the same, and more particularly, to a hot dip plated steel sheet having excellent platability and plating adhesiveness in which a steel sheet containing alloying elements forming oxides on a surface of the steel sheet at high temperatures is used as an underlying steel sheet, and a method of manufacturing the same. According to the present invention, a hot dip plated steel sheet having excellent platability and plating adhesiveness is provided, in which a steel sheet containing alloying elements forming oxides on a surface of the steel sheet at high temperatures is used as an underlying steel sheet, and thus, limitations in added amounts of silicon (Si), manganese (Mn), or aluminum (Al) may be mitigated. Therefore, development of new steels may be accelerated.

Description

technical field [0001] The present invention relates to a hot-dip-coated steel sheet for automotive materials and a manufacturing method thereof, and more particularly, to a hot-dip-coated steel sheet having excellent platability and plating adhesion, and its manufacture method. Background technique [0002] As environmental problems become increasingly severe, regulations on fuel economy of automobiles are also increasingly regulated, and therefore, various methods of reducing weight of automobiles have been sought as measures to improve fuel economy. [0003] To this end, steelmakers have worked to create high-strength steel to reduce the weight of steel sheets used in automotive materials while ensuring passenger safety. [0004] Under this trend, there has been an increasing demand for high-strength hot-dip galvanized (Zn) steel sheets for automobile bodies in recent years. However, conventional methods of producing high-strength steels using solid-solution strengtheni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/04C23C2/28C21D1/68
CPCC21D1/32C21D1/68C21D1/74C23C2/04C23C2/28C21D1/52Y10T428/12667Y10T428/1266C23C2/0222C23C2/0038C23C2/02C23C2/0224
Inventor 朴鲁范金钟常朴重喆李铃罗刘泓钟宣判禹韩相局
Owner POHANG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap