High-strength cold-rolled hot-galvanized dual-phase steel plate and manufacture method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and hot-dip galvanizing technology, applied in the direction of temperature control, etc., can solve difficulties, increase the difficulty of steelmaking, difficult to eliminate problems such as long-term Mn content, and achieve the effect of good matching of strength and ductility, and excellent plating performance.
Active Publication Date: 2015-03-11
ANGANG STEEL CO LTD
View PDF7 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although it is easy to obtain a typical dual-phase structure, it is very difficult to maintain 20-100s in the range of 454-493°C on the existing continuous hot-dip galvanizing production line, and the present invention does not take into account the lower heating and holding temperature, and it is difficult to eliminate Mn When the Mn content is large (such as the Mn content of the steel in the example reaches 1.81%), the banded structure formed mainly by cementite, pearlite, and bainite
At the same time, the invention does not mention how to produce cold-rolled substrates with suitable microstructure and good shape
[0006] The steel described in CA2564050A1 needs to add Mo, B, Ca, Cr, Ni, Nb, V, Ti and many other elements at the same time, and obtain a cold-rolled hot-dip galvanized dual-phase steel with a tensile strength of 440-780MPa through the hot-dip galvanizing process. More elements are added, which increases the difficulty of steelmaking and increases the manufacturing cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0042] Below in conjunction with specific embodiment the present invention is further described:
[0043] The composition of the steel of the embodiment is shown in Table 1, the hot rolling process parameters are shown in Table 2, the annealing and galvanizing process parameters and the mechanical properties of the steel plate after galvanizing are shown in Table 3, and the continuous annealing and galvanizing process system schematic diagram is shown in Table 3. figure 1 , the microstructure of the hot-rolled plate see figure 2 , the microstructure of cold-rolled hot-dip galvanized steel sheet see image 3 .
[0044] Chemical composition (mass fraction) % of table 1 embodiment steel
[0045]
[0046] The hot rolling process parameter of table 2 embodiment steel
[0047]
[0048] Table 3 Process parameters of annealing and galvanizing and mechanical properties of steel sheets after galvanizing
[0049]
[0050] Platability: The appearance of the coated steel shee...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
thickness
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a high-strength cold-rolled hot-galvanized dual-phase steel plate, characterized in that components, in mass percentage, are: 0.03% to 0.15% of C, less than or equal to 0.15% of Si, 1.00% to 1.75% of Mn, less than or equal to 0.015% of P, less than or equal to 0.012% of S, 0.02% to 0.15% of Al, 0.35% to 0.75% of Cr, 0.02% to 0.15% of Cu, 0.010% to 0.035% of Ti, less than or equal to 0.005% of N, in addition meeting the requirement that the total percentage of Mn, 1.29Cr and 0.46Cu is not less than 1.5% and not more than 2.5%, and the balance being Fe and inevitable impurities. The manufacture method comprises converter smelting, secondary refining, continuous casting, hot continuous rolling, cold acid continuous rolling, annealing galvanizing and hot dipping, wherein a galvanized substrate with a reasonable organization and composition and an excellent plate shape is obtained through controlled rolling and controlled cooling while rolling; and through employing a micro-slowly cooling way for heating from an end segment to an isothermal segment and a secondary fast cooling way for a fast cooling segment during continuous annealing galvanizing, the cold-rolled hot-galvanized dual-phase steel plate is obtained, wherein the steel plate is advantageous by having a tensile strength between 490 to 700 MPa, well-matched strength and ductility, an excellent coating performance, and a thickness between 0.5 to 2.5 mm, and can be used as an automobile cover component, an inner plate, a structural component, etc.
Description
technical field [0001] The invention belongs to the technical field of cold-rolled high-strength thin plates for automobiles, and provides a high-strength cold-rolled hot-dip galvanized dual-phase steel and a manufacturing method thereof. Background technique [0002] In recent years, with the continuous improvement of people's requirements for car crash safety and corrosion resistance, steel sheets for automobiles have developed towards high strength and full coating, which has prompted high-strength IF steels, bake-hardening steels, phase-transformation-induced plasticity steels and double-layer steels. The application of hot-dip galvanized high-strength steel such as phase steel in automobile body. At the same time, in order to reduce the greenhouse effect and protect the earth's environment, strengthen the control of CO 2 The limitation of emissions, which contributes to the lightweight of automobile bodies with low fuel consumption, has become an important research top...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.