Preparation method for novel rubber strip for sealing of automobile doors and windows and product

A technology for sealing rubber strips and products, which is applied in the field of rubber sealing materials, can solve the problems of further improvement in the aging resistance of products, high production costs of EPDM rubber sealing strips, and long vulcanization time. It is easy and excellent to achieve industrialization Effects of compression set, formulation and simplicity of production process

Inactive Publication Date: 2013-12-04
天津滨海新区大港汇丰汽车装饰有限公司
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, EPDM sealing strips for automobiles have defects such as high production cost, poor flame retardancy, long vulcanization time, and the aging resistance of products needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) Weigh 6Kg EPDM 4436, 5.5Kg EPDM 539, 10Kg carbon black, 3Kg light calcium carbonate, 9Kg paraffin oil, 0.5Kg zinc oxide, 0.1Kg stearic acid, 0.1Kg KY-405, 0.05Kg of MBZ, 0.1Kg of polyethylene glycol, 0.1Kg of polyethylene wax, 0.15Kg of AFLUX-42. In addition, weigh 0.15Kg accelerator CZ, 0.15Kg accelerator BZ, 0.05Kg accelerator TRA, 0.05Kg accelerator TT, 0.05Kg accelerator PZ, 0.1Kg sulfur, and 0.15Kg ammonium polyphosphate.

[0018] (2) Put ethylene propylene rubber in an internal mixer for 60 seconds, then add zinc oxide, stearic acid, KY-405, MBZ and mix for 40 seconds, add carbon black, light calcium carbonate, paraffin oil, Polyethylene glycol, polyethylene wax, and AFLUX-42 are banburyed for 120 seconds to obtain a section of glue. The temperature of mastication and mixing is controlled at 130°C.

[0019] (3) Put a section of rubber on the open mill, add accelerators CZ, BZ, TRA, TT, PZ, vulcanizing agent sulfur and flame retardant ammonium polyphosphate, ...

Embodiment 2

[0022] (1) Weigh 6Kg EPDM 4436, 5.5Kg EPDM 539, 12Kg carbon black, 3.3Kg light calcium carbonate, 9Kg paraffin oil, 0.5Kg zinc oxide, 0.15Kg stearic acid, 0.1Kg KY-405, MBZ 0.05Kg, Polyethylene Glycol 0.1Kg, Polyethylene Wax 0.1Kg, AFLUX-42 0.15Kg. In addition, weigh 0.2Kg accelerator CZ, 0.15Kg accelerator BZ, 0.05Kg accelerator TRA, 0.05Kg accelerator TT, 0.05Kg accelerator PZ, 0.1Kg sulfur, and 0.15Kg TCEP.

[0023] (2) Put ethylene propylene rubber in an internal mixer for 80 seconds, then add zinc oxide, stearic acid, KY-405, MBZ and mix for 40 seconds, add carbon black, light calcium carbonate, paraffin oil, Polyethylene glycol, polyethylene wax, and AFLUX-42 are banburyed for 120 seconds to obtain a section of glue. The temperature of mastication and mixing is controlled at 120°C.

[0024] (3) Put a section of rubber on the open mill, add accelerators CZ, BZ, TRA, TT, PZ, vulcanizing agent sulfur and flame retardant ammonium polyphosphate, and knead at 60°C until the ...

Embodiment 3

[0027] (1) Weigh 6Kg EPDM 4436, 5Kg EPDM 539, 12.5Kg carbon black, 4Kg light calcium carbonate, 9Kg paraffin oil, 0.5Kg zinc oxide, 0.15Kg stearic acid, 0.1Kg KY-405, 0.05Kg of MBZ, 0.1Kg of polyethylene glycol, 0.1Kg of polyethylene wax, 0.15Kg of AFLUX-42. In addition, weigh 0.2Kg accelerator CZ, 0.15Kg accelerator BZ, 0.05Kg accelerator TRA, 0.05Kg accelerator TT, 0.05Kg accelerator PZ, 0.2Kg sulfur, and 0.2Kg TCPP.

[0028] (2) Put ethylene propylene rubber in an internal mixer for 70 seconds, then add zinc oxide, stearic acid, KY-405, MBZ and mix for 30 seconds, add carbon black, light calcium carbonate, paraffin oil, Polyethylene glycol, polyethylene wax, and AFLUX-42 are banburyed for 120 seconds to obtain a section of glue. The temperature of mastication and mixing is controlled at 130°C.

[0029] (3) Put a section of rubber on the open mill, add accelerators CZ, BZ, TRA, TT, PZ, vulcanizing agent sulfur and flame retardant ammonium polyphosphate, and knead at 55°C u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method for a novel rubber strip for sealing of automobile doors and windows and a product. The preparation method employs ethylene propylene diene monomers as basic materials with cooperation of certain amounts of carbon black, calcium carbonate, paraffin oil, zinc oxide, stearic acid, polyvinyl alcohol, high-molecular wax, compound antioxidants, dispersants, compound accelerants, vulcanizing agents, fire retardants and the like. The above materials are subjected to mixing, open milling and vulcanization technologies to obtain the rubber strip. The preparation method has advantages of simple formula, simple production technology, short vulcanizing time, high production efficiency, relatively low production cost, easy industrialization enforcement and the like. The rubber product for sealing is advantaged by good sealing performance, uniform structure, resistance to corrosion, resistance to high and low temperature, flame resistance, environment protection and comfort.

Description

technical field [0001] The invention relates to the field of rubber sealing materials, in particular to a preparation method and a product thereof of a novel rubber strip for automobile door and window sealing, which has good sealing performance, uniform structure, corrosion resistance, high and low temperature resistance, flame retardancy and environmental protection. Background technique [0002] In the modern industrial field, sealing technology plays a pivotal role, and sealing failure will not only greatly increase subsequent maintenance costs, but may also lead to fatal disasters. Material properties are the decisive factors for the performance of sealing products. In the field of automobiles, sealing materials are mainly used in three aspects: oil seals, water seals and air seals. Among them, automobile door and window sealing strips are important air seal and water seal components. They are widely used in car doors, windows, skylights and other parts. They have sound...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08K13/02C08K3/04C08K3/26C08K3/22C08K5/09C08K5/18C08K5/37C08K5/47C08K5/39C08K5/40C08K3/06C08K3/32C08K5/521C08K5/523B29B7/28B29B7/72B29C35/02
Inventor 顾孟良
Owner 天津滨海新区大港汇丰汽车装饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap