Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating

A kind of fire retardant coating, ultra-thin technology, applied in the direction of fire retardant coatings, coatings, etc., can solve the problems of potential safety hazards, damage to human health, and can not play a role in preventing hydrocarbon fires, etc.

Active Publication Date: 2016-05-11
石家庄雅致化工有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although its comprehensive performance is good, there are disadvantages such as waste of resources, pollution of the environment, damage to human health, and potential safety hazards. High temperature and quickly burned, but can not play a role in preventing hydrocarbon fires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating
  • Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating
  • Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating, the raw material composition includes A component and B component, of which A component includes high chlorinated polyethylene, tetrabromobisphenol, ammonium polyphosphate, melamine, pentaerythritol, antimony trioxide , chlorinated paraffin, titanium dioxide, mixed solvent, component B is polyamide 300#; components A and B are mixed at a mass ratio of 1.5:9.2;

[0020] The content of each component by mass percentage in component A is as follows:

[0021]

[0022] Wherein the mixed solvent comprises: cyclohexanone: butanol: butyl acetate: ethyl acetate, the mass ratio is: 1:0.6:0.5:1.

Embodiment 2

[0024] Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating, the raw material composition includes A component and B component, of which A component includes high chlorinated polyethylene, tetrabromobisphenol, ammonium polyphosphate, melamine, pentaerythritol, antimony trioxide , chlorinated paraffin, titanium dioxide, mixed solvent, component B is polyamide 300#; components A and B are mixed at a mass ratio of 1.5:9.4;

[0025] The content of each component by mass percentage in component A is as follows:

[0026]

[0027]

[0028] Wherein the mixed solvent includes: cyclohexanone: butanol: butyl acetate: ethyl acetate, the mass ratio is: 1:0.5:0.7:1.2.

Embodiment 3

[0030] Hydrocarbon-resistant indoor ultra-thin steel structure fireproof coating, the raw material composition includes A component and B component, of which A component includes high chlorinated polyethylene, tetrabromobisphenol, ammonium polyphosphate, melamine, pentaerythritol, antimony trioxide , chlorinated paraffin, titanium dioxide, mixed solvent, component B is polyamide 300#; components A and B are mixed at a mass ratio of 1.5:9.8;

[0031] The content of each component by mass percentage in component A is as follows:

[0032]

[0033] Wherein the mixed solvent comprises: cyclohexanone: butanol: butyl acetate: ethyl acetate, the mass ratio is: 1: (0.5-0.8): (0.5-0.8): (1-1.2).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hydrocarbon-resistant indoor ultrathin fireproofing coating for steel structures. The fireproofing coating consists a component A and a component B, wherein the component A is composed of highly chlorinated polyethylene, TBBP, ammonium polyphosphate, melamine, pentaerythritol, antimonous oxide, chlorinated paraffin, titanium dioxide and a mixed solvent, and the component B is polyamide 300#, and the components A and B are mixed at 1.5:(9-10) in percentage by mass. The fireproofing coating has characteristics of strong adhesion force, good film forming performance, excellent combustion and expansion, high hardness of carbon layer, being anti-corrosive and anti-rust, hydrocarbon fire resistance and the like, and the fireproofing coating is free from toxicity, smell and release of harmful gas.

Description

technical field [0001] The invention relates to the technical field of metal surface coatings, in particular to a hydrocarbon-resistant indoor ultra-thin fireproof coating for steel structures. Background technique [0002] Most of the frames of modern high-rise and large buildings use steel structures, but steel as a building material has unavoidable defects in fire protection, such as yield point, tensile strength and modulus of elasticity, etc. will drop sharply due to the increase of temperature, thus The loss of bearing capacity can easily cause the collapse of the building. Therefore, it is often necessary to apply fire-resistant coatings to construction steel to ensure construction quality and durability. [0003] There are many types of fireproof coatings for steel structures, which are mainly divided into three types: thick, thin and ultra-thin according to the thickness of the coating. Among them, thin and ultra-thin fireproof coatings have become fireproof due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D123/28C09D5/18
Inventor 王海辉
Owner 石家庄雅致化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com