Nano-polypropylene flame retardant plastic

A flame-retardant plastic and nano-flame retardant technology, applied in the field of plastic film, can solve the problems of not being able to reduce the thermal deformation temperature, mechanical temperature and electrical insulation performance of plastic products, not affecting the mechanical strength of plastics, and being unable to provide, so as to increase the reactivity point, low product cost, and the effect of preventing temperature rise

Inactive Publication Date: 2013-12-25
SUZHOU XIANGYUAN SPEICAL FINE CHEM
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (2) After the flame retardant is added, it cannot affect the mechanical strength of the plastic, especially it cannot reduce the thermal deformation temperature, mechanical temperature and electrical insulation performance of the plastic product;
Mechanisms such as: protective film mechanism, otherwise gas mechanism, cooling mechanism, and termination chain reaction mechanism are given in existing textbooks. These can provide a vague direction for the selection of flame retardants, but they cannot provide real effective information. s help

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048]A kind of polypropylene flame-retardant plastics, is made up of following components by weight

[0049] Polypropylene 60 parts

[0050] Polyethylene 20 parts

[0051] 20 parts of terpene resin

[0052] 10 parts polystyrene

[0053] 10 parts of nitrile rubber

[0054] Dibutyl sebacate 5 parts

[0055] 5 parts polyimide

[0056] 10 parts liquid paraffin

[0057] 10 parts of antimony trioxide

[0058] Nano titanium oxide 10 parts

[0059] Zinc stearate 10 parts

[0060] Flame retardant 20 parts

[0061] Antioxidant 0.1 parts

[0062] 0.5 parts of defoamer

[0063] Auxiliary 1 part

[0064] 25-30 parts of nano flame retardant compound;

[0065] The preparation method of described nano flame retardant composite agent is:

[0066] (1) The silicon hydroxyapatite, red phosphorus, attapulgite, hydrotalcite, montmorillonite, titanium dioxide, calcite, kaolin according to 25-35: 15-20: 10-15: 10-15: 8-10: 8-10: 7-8: 5-7 parts by mass, mixed, added to a mixed solution...

Embodiment 2

[0078] A kind of polypropylene flame-retardant plastics, is made up of following components by weight:

[0079] 80 parts of polypropylene

[0080] Polyethylene 50 parts

[0081] 30 parts of terpene resin

[0082] 30 parts polystyrene

[0083] 25 parts of nitrile rubber

[0084] Dibutyl sebacate 10 parts

[0085] 10 parts polyimide

[0086] 20 parts liquid paraffin

[0087] 15 parts of antimony trioxide

[0088] 30 parts of nano-titanium oxide

[0089] Zinc stearate 22 parts

[0090] Flame retardant 40 parts

[0091] Antioxidant 0.3 parts

[0092] 1 part defoamer

[0093] Auxiliary 3 parts

[0094] 25-30 parts of nano flame retardant compound;

[0095] The preparation method of described nano flame retardant composite agent is:

[0096] (1) The silicon hydroxyapatite, red phosphorus, attapulgite, hydrotalcite, montmorillonite, titanium dioxide, calcite, kaolin according to 25-35: 15-20: 10-15: 10-15: 8-10: 8-10: 7-8: 5-7 parts by mass, mixed, added to a mixed sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a nano-polypropylene flame retardant plastic which consists of the following components in parts by weight: 60-80 parts of polypropylene, 20-50 parts of polyethylene, 20-30 parts of terpene resin, 10-30 parts of polystyrene, 10-25 parts of nitrile rubber, 5-10 parts of dibutyl sebacate, 5-10 parts of polyimide, 10-20 parts of liquid paraffin, 10-15 parts of antimonous oxide, 10-30 parts of nano-titanium oxide, 10-22 parts of zinc stearate, 20-40 parts of a flame retardant, 0.1-0.3 part of an antioxidant, 0.5-1 part of a defoamer, 1-3 parts of an assistant and the like.

Description

technical field [0001] The invention relates to a plastic film, in particular to an antibacterial, high-strength talcum powder modified polypropylene plastic. Background technique [0002] Plastic is a polymer material with special properties. It has the characteristics of light weight, good chemical stability, corrosion resistance, good insulation, convenient molding, and low cost. It is widely used in electronics industry, automobile manufacturing, aerospace, industry and other fields. . However, plastics are flammable and burn quickly, producing a large amount of toxic gases. According to statistics, casualties caused by suffocation and smoke poisoning in fires account for 50-80% of the total number of casualties in fires. In recent years, the rapid development of electronics, construction, aviation and automobile industries has put forward higher requirements on the performance of plastics. Among them, flame-retardant plastics are not easy to burn, have low flame prop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L45/00C08L25/06C08L9/02C08L79/08C08K13/06C08K3/34C08K5/5419C08K5/3492C08K3/22C08K3/32
Inventor 周建颜玉荣
Owner SUZHOU XIANGYUAN SPEICAL FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap