A preparation method of a modified iron-silicon-boron soft magnetic powder core with a magnetic permeability of 50

A technology of soft magnetic powder core and iron silicon boron is applied in the field of preparation of modified iron silicon boron soft magnetic powder core to achieve the effects of easy operation, improvement of noise defects and noise reduction

Active Publication Date: 2016-01-20
QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the above problems, the object of the present invention is to provide a method for preparing a modified iron-silicon-boron soft magnetic powder core with a magnetic permeability of 50, to improve the noise defects of the iron-silicon-boron soft magnetic powder core, and to improve its high-frequency characteristics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of the modified FeSiB soft magnetic powder core provided in this embodiment includes the following steps,

[0027] Step 1, embrittlement treatment: heat-treat the iron-silicon-boron amorphous metal strip at 300°C for 2 hours to make it embrittled and easily crushed;

[0028] Step 2, crushing: crushing the brittle amorphous metal strip to obtain amorphous metal powder;

[0029] Step 3, sieving and proportioning: sieve the amorphous metal powder, and then mix it into a first powder with a weight content of 30% passing through -200~+270 mesh, and a weight content of 40% passing through- Powder particles composed of the second powder of 270~+325 mesh and powder particles composed of the third powder passing through -325~+500 mesh with a weight content of 30%;

[0030] Step 4, passivation treatment and insulation coating: Pour the proportioned amorphous powder particles into the mixer, stir and mix evenly, then add phosphoric acid solution for passiva...

Embodiment 2

[0053] The preparation method of the modified iron-silicon-boron soft magnetic powder core provided in this embodiment includes the following steps:

[0054] Step 1, embrittlement treatment: heat treatment of the iron-silicon-boron amorphous metal ribbon at 300° C. for 2 hours to make it embrittled and easy to crush;

[0055] Step 2, pulverizing: pulverizing the embrittled amorphous metal ribbon to obtain amorphous metal powder;

[0056] Step 3, sieving and proportioning: the amorphous metal powder is sieved, and then mixed into a first powder with a weight content of 20 to 40% that passes through a -200 to +270 mesh, and a weight content of 30 to 50. % powder particles composed of the second powder passing through the -270~+325 mesh and powder particles composed of the third powder passing through the -325~+500 mesh with a weight content of 10~50%;

[0057] Step 4, passivation treatment and insulation coating: pour the well-proportioned amorphous powder particles into the mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of metal soft magnetic material manufacturing, and particularly relates to a method for manufacturing a modified silicon iron boron soft magnetic powder core with magnetic conductivity of 50. The method comprises the first step of embrittlement treatment, the second step of crushing, the third step of screening and matching, the fourth step of passivating treatment and insulation covering, the fifth step of modifying agent adding, the sixth step of compression moulding and the seventh step of annealing treatment and spraying. According to the method, the noise defect of the silicon iron boron soft magnetic powder core can be overcome, and the high-frequency performance of the silicon iron boron soft magnetic powder core can be improved.

Description

technical field [0001] The invention belongs to the field of metal soft magnetic material manufacturing, and in particular relates to a method for preparing a modified iron-silicon-boron soft magnetic powder core with a magnetic permeability of 50. Background technique [0002] Since Professor Duwez in the United States invented the rapid quenching process to prepare amorphous alloys in 1960, due to its unique structure, efficient preparation process, excellent material properties and broad application prospects, it has been favored by material scientists and the industry. of special attention. Amorphous magnetic powder core is a new type of composite electronic material, mainly used in switching power supply cores, common-mode inductors, high-frequency inverters and zero-sequence transformers. [0003] At present, the magnetic powder core products mainly include iron silicon boron magnetic powder cores, sendust magnetic powder cores, iron nickel magnetic powder cores, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/02H01F1/147H01F1/24B22F9/04B22F1/02B22F3/02
Inventor 纪杰江志滨王亚娜李维强姜海滨
Owner QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap