Flame-retardant fabric

A flame retardant fabric and polyester flame retardant technology, applied in the field of textile fabrics, can solve the problems of secondary damage caused by dripping and melting, and achieve the effect of high efficiency flame retardant performance

Inactive Publication Date: 2014-02-05
SUZHOU WILDER IND & TRADE
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The main problem with the existing flame-retardant fabrics is that the weaving yarn is a polymeric plastic material, which is prone to dripping and melting to cause secondary damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The polyphenylene sulfide fiber and bamboo fiber are blended into weft yarn according to the mass ratio of 60% and 40% respectively.

[0014] The warp yarn of 110dtex flame-retardant polyester fiber and the weft yarn of polyphenylene sulfide fiber blended yarn are interwoven in a plain weave structure, and finally a flame-retardant fabric with durable flame-retardant effect is woven.

Embodiment 2

[0016] The polyphenylene sulfide fiber and bamboo fiber are blended into weft yarn according to the mass ratio of 80% and 20% respectively.

[0017] The 167dtex flame-retardant polyester fiber warp and polyphenylene sulfide fiber blended yarn weft are interwoven in a plain weave structure, and finally a flame-retardant fabric with a durable flame-retardant effect is woven.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant fabric which comprises warp yarns and weft yarns by interweaving, wherein the warp yarns are made of flame-retardant polyester fibers, and the weft yarns are polyphenylene sulfide fiber blended yarns. The flame-retardant fabric is comfortable, breathable, antibacterial and free of pungent smell, and has durable and efficient flame resistance.

Description

Technical field: [0001] The invention relates to the technical field of textile fabrics, in particular to a flame-retardant fabric. Background technique: [0002] At present, flame-retardant fabrics on the market are divided into two types: permanent flame-retardant fabrics and disposable flame-retardant fabrics. It plays a lot of roles in the field of protective clothing. The flame-retardant protective clothing made of flame-retardant fabric has excellent washing resistance, non-toxic, tasteless and non-irritating, safe and reliable to the human body, breathable and moisture-permeable, soft to the touch, and comfortable to wear. [0003] The main problem of existing flame-retardant fabrics is that the weaving yarn is a polymeric plastic material, which is prone to dripping and melting to cause secondary damage. Therefore, it is necessary to develop a highly efficient flame-retardant fabric to overcome the damage caused by dripping again. Invention content: [0004] The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D03D15/12D02G3/04D03D15/217D03D15/225D03D15/283D03D15/47D03D15/513
Inventor 刘玲
Owner SUZHOU WILDER IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap