Rare earth doped lutetium lithium fluoride nanomaterials and its preparation and application

A rare earth doping, lutetium lithium fluoride technology, applied in luminescent materials, material excitation analysis, chemical instruments and methods, etc., can solve the problem of little research on lutetium lithium fluoride, etc. The effect of uniform and controllable particle size

Active Publication Date: 2019-04-16
FUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the research on rare earth doped fluorides mainly focuses on sodium yttrium fluoride (NaYF 4 ), sodium gadolinium fluoride (NaGdF 4 ) or lithium yttrium fluoride (LiYF 4 ) and other systems, for lithium lutetium fluoride (LiLuF 4 ) is rarely studied
However, there are no reports on the synthesis, optical properties and applications of monodisperse water-soluble rare earth-doped lithium lutetium fluoride nano-fluorescence labeling materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth doped lutetium lithium fluoride nanomaterials and its preparation and application
  • Rare earth doped lutetium lithium fluoride nanomaterials and its preparation and application
  • Rare earth doped lutetium lithium fluoride nanomaterials and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0036] Example 1: LiLuF 4 : Preparation of 1%Er, 20%Yb nanoparticles. Weigh 0.120g Li(CF 3 COO) 2 ·H 2 O, 0.449gLu(CH 3 COO) 3 4H 2 O, 0.006g Er(CH 3 COO) 3 4H 2 O and 0.113g Yb(CH 3 COO) 3 4H 2 O, then add 6mL oleic acid, 6mL oleylamine and 2mL octadecene, heat to 120°C with nitrogen gas and keep it warm for 30 minutes to form a transparent solution. And washing to get about 28nm oil-soluble LiLuF 4 : 1% Er, 20% Yb nanoparticles. Add 112 μL of concentrated hydrochloric acid to 15 mL of absolute ethanol to prepare an acidic solution of pH 1. Disperse oil-soluble nanocrystals in the above-mentioned acidic ethanol solution, centrifuge after ultrasonication for 30 minutes, and alternately wash several times with absolute ethanol and water to obtain water-soluble LiLuF of about 28 nm. 4 : 1%Er, 20%Yb nanocrystals.

example 2

[0037] Example 2: LiLuF 4 : Preparation of 0.5%Tm, 20%Yb nanoparticles. Weigh 0.120g Li(CF 3 COO) 2 ·H 2 O, 0.452g Lu(CH 3 COO) 3 4H 2 O, 0.003g Tm(CH 3 COO) 3 4H 2 O and 0.113g Yb(CH 3 COO) 3 4H 2 O, then add 6mL oleic acid, 6mL oleylamine and 2mL octadecene, heat to 120°C with nitrogen gas and keep it warm for 30 minutes to form a transparent solution. And washing to get about 28nm oil-soluble LiLuF 4 : 0.5%Tm, 20%Yb nanoparticles. Disperse the oil-soluble nanocrystals in the acidic ethanol solution as described in Example 1, centrifuge after ultrasonication for 30 minutes, and alternately wash several times with absolute ethanol and water to obtain a water-soluble LiLuF of about 28 nm. 4 : 0.5%Tm, 20%Yb nanocrystals.

[0038] Example 3: LiLuF 4 : 1%Er, 20%Yb@LiLuF 4 Preparation of 8-layer coated core-shell nanoparticles. First, weigh 0.120g Li(CF 3 COO) 2 ·H 2 O and 0.568g Lu(CH 3 COO) 3 4H 2 O, then add 9 mL of oleic acid, 9 mL of oleylamine and 2 m...

example 6

[0041] Example 6: LiLuF 4 : 0.5%Tm, 20%Yb@LiLuF 4 Preparation of 16-layer coated core-shell nanoparticles. First, weigh 0.240g Li(CF 3 COO)2 ·H 2 O and 1.136g Lu(CH 3 COO) 3 4H 2 O, then add 18mL oleic acid, 18mL oleylamine and 4mL octadecene, heat to 120°C with nitrogen gas and keep it warm for 30 minutes to form a transparent solution, then cool down to room temperature to obtain shell layer precursor solution A. As described in Example 2, the temperature was raised to 320°C for 40 minutes to form a solution B, and 2mL of A was injected into B, and kept at 320°C for 10 minutes; then 2mL of A was injected again, and the temperature was kept at 320°C for 10 minutes; after 16 cycles of this Cool down to room temperature, add 30mL acetone to precipitate, separate and wash to obtain about 50nm oil-soluble LiLuF 4 : 0.5%Tm, 20%Yb@LiLuF 4 16 layers of coated core-shell nanoparticles. Disperse the oil-soluble nanocrystals in the acidic ethanol solution as described in Examp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rare earth-doped lithium lutetium fluoride nano-material, and a preparation method and an application thereof. The material is obtained by doping Yb / Er(20 / 1%) or Yb / Tm(20 / 0.5%) luminescent ions into a lithium lutetium fluoride matrix, can emit visible light under the excitation of 980nm infrared light, and can be used for the up-conversion heterogeneous detection and cell imaging through the connection with biological molecules. Additionally, heavy rare earth ions in the matrix also have a strong X-ray attenuation capability, and can be used as a computer tomography imaging contrast agent. The invention also provides the preparation method of the nano-material. The nano-material has a water solubility and excellent performances, so the nano-material can be applied in the fields of the biological detection, the biological imaging and the like.

Description

technical field [0001] The invention relates to the field of nano-luminescent materials, in particular to a rare-earth nano-luminescent material that can be used for biological detection and imaging and a preparation method thereof. Background technique [0002] In recent years, rare earth-doped upconversion luminescent nanomaterials have shown great application value in photoconductive switches, information storage, optoelectronic devices, and solar cells, among which the most notable is the recent rise of rare earth-doped upconversion luminescent nanomaterials. Applications of materials in fluorescent biomarkers. Compared with traditional fluorescent labeling materials (such as fluorescent dyes and quantum dots), rare earth-doped upconversion luminescent nanomaterials not only have high chemical stability, long fluorescence lifetime, and low potential biological toxicity, but also have a large It has significant advantages such as high light penetration depth, no autofluo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C09K11/85G01N21/64
Inventor陈学元黄萍郑伟涂大涛朱浩淼
OwnerFUJIAN INST OF RES ON THE STRUCTURE OF MATTER CHINESE ACAD OF SCI